Electrochemical And Spectroscopic Studies Of Ethanol Oxidation On Nano-Cubic Pt Modified By Tin Adatoms, Lu Rao, Bin-Wei Zhang, Yan-Yan Li, Yan-Xia Jiang, Shi-Gang Sun
Electrochemical And Spectroscopic Studies Of Ethanol Oxidation On Nano-Cubic Pt Modified By Tin Adatoms, Lu Rao, Bin-Wei Zhang, Yan-Yan Li, Yan-Xia Jiang, Shi-Gang Sun
Journal of Electrochemistry
The nano-cubic Pt modified by tin (Sn) was synthesized and used to investigate the role of this adatom played in the ethanol oxidation. The onset potential of ethanol oxidation was significantly shifted negatively which can be forward about 300 mV when the coverage of Sn (θSn)was 0.9. The electrtochemical in situ FTIR result demonstrated that the amount of CO2 increased first, and then decreased with θSn increased, and reached the maximun when θSn was 0.38. Furthermore, the formation of acetic acid could be observed at very low potential (-0.05 V) after modifying Sn adatom, and the amount of acetic acid …
Synthesis Of Platinum Nanocrystallites And Possible Electrocatalytic Properties For Methanol, Lei-Lei Lu, Bao-Zhong Du, Sha Sun, Jin-Fen Niu, Jie Zhao
Synthesis Of Platinum Nanocrystallites And Possible Electrocatalytic Properties For Methanol, Lei-Lei Lu, Bao-Zhong Du, Sha Sun, Jin-Fen Niu, Jie Zhao
Journal of Electrochemistry
Platinum nanocrystallites were synthesized by the colloidal method using oxamide as the stabilizer. The morphologies and electrocatalytic performances for methanol of platinum nanocrystallites prepared at different pH values and with different reactant ratios of precursor and stabilizer were investigated. It was found that the platinum nanocrystallites synthesized at pH=5 and with the reactant ratio of 1:20 showed the best electrocatalytic activity for methanol. The peak current density reached up to 1709 μA·cm-2. Furthermore, the electrocatalytic activity of platinum nanocrystallites for methanol reduced significantly although the cyclic voltammograms in the blank solution were not obviously changed after exposing in …
Pulse Electrodeposition Of Pd-Ni Alloy Nanoparticles For Electrocatalytic Oxidation Of Formic Acid, Fang-Zu Yang, Jun-Pei Yue, Zhong-Qun Tian, Shao-Min Zhou
Pulse Electrodeposition Of Pd-Ni Alloy Nanoparticles For Electrocatalytic Oxidation Of Formic Acid, Fang-Zu Yang, Jun-Pei Yue, Zhong-Qun Tian, Shao-Min Zhou
Journal of Electrochemistry
The Pd-Ni alloy nanoparticles with nickel atomic contents of 12.0%, 16.4% and 22.6% were successfully electrodeposited from a Pd-Ni alloy electrolyte by square wave pulse plating. The alloy nanoparticles were in the spherical shape with a diameter of 50 ~ 80 nm. As the growth potential of the alloy was negatively shifted, the nickel content of the alloy was increased, and the size of the nanoparticles was almost the same, whereas the number, the degree of crosslinking and the real active area of the nanoparticles were increased. As the nickel content of the alloy nanoparticles increased, the peak current for …