The structure of the type I tetraheme cytochrome c3 from Desulfovibrio desulfuricans G20 was determined to 1.5 A˚ by X-ray crystallography. In addition to the oxidized form, the structure of the molybdate-bound form of the protein was determined from oxidized crystals soaked in sodium molybdate. Only small structural shifts were obtained with metal binding, consistent with the remarkable structural stability of this protein. In vitro experiments with pure cytochrome showed that molybdate could oxidize the reduced cytochrome, although not as rapidly as U(VI) present as uranyl acetate. Alterations in the overall conformation and thermostability of the metal-oxidized protein were investigated …

Corrosion Barrier Development For Lbe Corrosion Resistance: Quarterly Report (April 2006), Biswajit Das

Transmutation Sciences Materials (TRP)

As reported in the last quarterly report, synthesis of Cr nanowires was found to be problematic in terms of uniform coverage. Hence Ni was identified as the alternative metal to form the nanowires. The purpose of the metal nanowires is to provide structural integrity to the nanoporous alumina, as well as a second defense mechanism against corrosion by oxidizing in case the top alumina layer is compromised. Nickel was selected due to its established electrochemical synthesis procedure. While Ni can provide very good structural integrity to the porous alumina, one potential problem is its higher dissolution rate in LBE. However, …

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications, Biswajit Das

Transmutation Sciences Materials (TRP)

Advanced transmutation systems require structural materials that are able to withstand high neutron fluxes, high thermal cycling, and high resistance to chemical corrosion. The current candidate materials for such structures are ferritic and ferritic-martensitic steels due to their strong resistance to swelling, good microstructural stability under irradiation, and the retention of adequate ductility at typical reactor operating temperatures.

In parallel, lead bismuth eutectic (LBE) has emerged as a potential spallation target material for efficient production of neutrons, as well as a coolant in the accelerator system. While LBE has excellent properties as a nuclear coolant, it is also highly corrosive …