Synthesis Of Mild–Hard Aao Templates For Studying Magnetic Interactions Between Metal Nanowires, Jin-Hee Lim, Aurelian Rotaru, Seong-Gi Min, Leszek Malkinski, John B. Wiley
Synthesis Of Mild–Hard Aao Templates For Studying Magnetic Interactions Between Metal Nanowires, Jin-Hee Lim, Aurelian Rotaru, Seong-Gi Min, Leszek Malkinski, John B. Wiley
Physics Faculty Publications
The sequential application of mild and hard anodization techniques in the fabrication of porous aluminamembranes allows one to decrease the number of continuous pores in anodized aluminium oxide (AAO) templates. Initially, standard mild anodization techniques were used to create porous templates with 100 nm interpore distances and 70 nm pore diameters. Hard anodization treatment on the same membrane then produced interpore distances of about 265 nm with diameters of 110 nm. At the interface between the two anodization steps, many of the mild-side pores were terminated to create a mild–hard membrane (Mi–Ha AAO) where the functional interpore distances were 200–300 …
Ultrafine Nife2o4 Powder Fabricated From Reverse Microemulsion Process, Jiye Fang, Narayan Shama, Le Duc Tung, Eun Young Shin, Charles J. O'Connor, Kevin L. Stokes, Gabriel Caruntu, John B. Wiley, Leonard Spinu, Jinke Tang
Ultrafine Nife2o4 Powder Fabricated From Reverse Microemulsion Process, Jiye Fang, Narayan Shama, Le Duc Tung, Eun Young Shin, Charles J. O'Connor, Kevin L. Stokes, Gabriel Caruntu, John B. Wiley, Leonard Spinu, Jinke Tang
Physics Faculty Publications
NiFe2O4 ultrafine powder with high crystallinity has been prepared through a reverse microemulsion route. The composition in starting solution was optimized, and the resulting NiFe2O4 was formed at temperature of around 550–600 °C, which is much lower than that observed from the solid-state reaction. Magnetic investigation indicates that samples are soft-magnetic materials with low coercivity and with the saturation magnetization close to the bulk value of Ni ferrite.