Nanoscience and Nanotechnology Commons^™

Photoelectrochemical Properties Of Tio_2 Nanoparticles, Jie Qu, Ying Li, Qi-Wei Jiang, Xue-Ping Gao

Journal of Electrochemistry

The protonated titanate nanoparticles were obtained at room temperature and subsequently calcined at different temperatures(300 ℃,400 ℃,500 ℃,600 ℃ and 700 ℃) in air.The obtained products were characterized by XRD,TEM and UV-Vis.It is found that the grain sizes of TiO2 nanoparticles calcined at 300 ℃ were about 20 nm,and increased gradually with the temperature rise.Photoelectric performance was measured with I～V curve and electrochemical impedance spectroscopy(EIS).The TiO2 nanoparticles obtained at 500 ℃ showed the best photoelectrochemical properties with a photovoltaic conversion efficiency of 6.39%,which is much higher than those at other temperatures.In addition,it is also demonstrated that the charge transfer resistance …

Rhodium Nanoparticle Shape Dependence In The Reduction Of No By Co, James Russell Renzas, Yawen Zhang, Wenyu Huang, Gabor Somoraji

Wenyu Huang

The shape dependence of the catalytic reduction of nitric oxide by carbon monoxide on rhodium nanopoly- hedra and nanocubes was studied from 230 to 270 ° C. The nanocubes are found to exhibit higher turnover frequency and lower activation energy than the nanopolyhedra. These trends are compared to previous studies on Rh single crystals.

Spectroscopic Investigation Of Palladium-Copper Bimetallic Systems For Pem Fuel Cell Catalysts, Timo Hofmann

UNLV Theses, Dissertations, Professional Papers, and Capstones

One of the main barriers to commercialization of polymer electrolyte membrane fuel cells systems is cost, which is largely due to the need of platinum (Pt)-containing catalysts. In this thesis we investigate bimetallic systems consisting of a base metal (copper) and a noble metal (palladium) that, as an alloy on the nanoscale, mimic the electronic properties that make Pt desirable as a catalyst.

We present a detailed investigation of the electronic structure of carbon-supported Pd/Cu nanoparticle catalysts, model bilayer thin film systems, alloys, and various metal reference samples. We have investigated the valence band structure of the catalysts using a …