Characterization Of Simulated Low Earth Orbit Space Environment Effects On Acid-Spun Carbon Nanotube Yarns, Ryan A. Kemnitz, Gregory R. Cobb, Abhendra K. Singh, Carl R. Hartsfield
Characterization Of Simulated Low Earth Orbit Space Environment Effects On Acid-Spun Carbon Nanotube Yarns, Ryan A. Kemnitz, Gregory R. Cobb, Abhendra K. Singh, Carl R. Hartsfield
Faculty Publications
The purpose of this study is to quantify the detrimental effects of atomic oxygen and ultraviolet (UV) C radiation on the mechanical properties, electrical conductivity, and piezoresistive effect of acid-spun carbon nanotube (CNT) yarns. Monotonic tensile tests with in-situ electrical resistance measurements were performed on pristine and exposed yarns to determine the effects of the atomic oxygen and UVC exposures on the yarn’s material properties. Both type of exposures were performed under vacuum to simulate space environment conditions. The CNT yarns’ mechanical properties did not change significantly after being exposed to UV radiation, but were significantly degraded by the atomic …
Quantifying The Effects Of Hyperthermal Atomic Oxygen And Thermal Fatigue Environments On Carbon Nanotube Sheets For Space-Based Applications, Jacob W. Singleton, Gregory R. Cobb, Heath E. Misak, Ryan A. Kemnitz
Quantifying The Effects Of Hyperthermal Atomic Oxygen And Thermal Fatigue Environments On Carbon Nanotube Sheets For Space-Based Applications, Jacob W. Singleton, Gregory R. Cobb, Heath E. Misak, Ryan A. Kemnitz
Faculty Publications
The effects of atomic oxygen and thermal fatigue on two different types of carbon nanotube sheets were studied. One set was treated with nitric acid, while the other set was left untreated. Monotonic tensile tests were performed before and after exposure to determine the effects of either exposure type on the sheets’ mechanical properties. Electrical conductivity and electromagnetic interference measurements were recorded to determine the effects of AO-exposure and thermal cycling on the sheets’ electrical properties. Neither exposure type affected the sheets’ specific strengths. Both exposure types increased the sheets’ specific stiffnesses and decreased the sheets’ strains at failure. The …