Control Of High-Temperature Static And Transient Thermomechanical Behavior Of Simo Ductile Iron By Al Alloying, Semen Naumovich Lekakh, Catherine E. Johnson, L. Godlewski, Mei Li

Materials Science and Engineering Faculty Research & Creative Works

Silicon and molybdenum (SiMo) ductile iron is commonly used for exhaust manifolds because these components experience thermal cycling in oxidizing environment, which requires resistance to fatigue during transient thermomechanical loads. Previous studies have demonstrated that alloying elements, such as Al, to SiMo ductile iron reduces the amount of surface degradation during static high-temperature exposure. However, deterioration of sphericity of the graphite nodules and a decrease in ductility could affect the tendency of cracking during thermal cycling. In this article, the effect of Al alloying on static and transient thermomechanical behavior of SiMo ductile iron was investigated to optimize the amount …