Analysis Of Fatigue Crack Propagation In Welded Steels, Roberto Angelo Demarte
Analysis Of Fatigue Crack Propagation In Welded Steels, Roberto Angelo Demarte
Master's Theses (2009 -)
This thesis presents the study of fatigue crack propagation in a low carbon steel (ASTM A36) and two different weld metals (AWS A5.18 and AWS A5.28). Fatigue crack propagation data for each weld wire is of interest because of its use for predicting and analyzing service failures. Fatigue crack growth test specimens were developed and fabricated for the low carbon steel base metal and for each weld wire. Weld specimens were stress relieved prior to fatigue testing. Specimens were tested on a closed-loop servo hydraulic test machine at two different load ratios. Fatigue test data was collected to characterize both …
The Effect Of Cryogenic Treatment On The Fatigue Life Of Chrome Silicon Steel Compression Springs, Debra Lynn Smith
The Effect Of Cryogenic Treatment On The Fatigue Life Of Chrome Silicon Steel Compression Springs, Debra Lynn Smith
Dissertations (1934 -)
The purpose of this dissertation is to explore the effect of cryogenic treatment on the fatigue life of compression springs. Product manufacturers are constantly searching for ways to make their products last longer. This dissertation addresses three questions: (1) What is the effect of cryogenic treatment on the fatigue life of chrome silicon steel compression springs? Does the life increase, decrease, or remain the same? (2) What is the effect of cryogenic treatment on the Percent Load Loss (Stress Relaxation) of chrome silicon steel compression springs? (3) What are the possible changes in the material that cause these effects?
The …