Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC) and localized corrosion behavior of Type 422 stainless steel in aqueous environments at ambient and elevated temperature. The results of constant load SCC testing using smooth specimens showed no failure in the neutral solution but a threshold stress of 97 ksi was observed in the 90°C acidic environment. SCC testing by the slow-strain-rate test method indicate that the time-to-failure, true failure stress and ductility parameters were gradually reduced with increasing temperature, showing more pronounced effect in the acidic solution. The application of a controlled cathodic potential showed further …