The Effect Of Isostatic Pressing On The Dielectric Properties Of Screen Printed Ba0.5Sr0.5Tio3 Thick Films, Siwei Wang, Lingling Zhang, Jiwei Zhai, Fanglin Chen

Faculty Publications

Ba_0.5Sr_0.5TiO₃ thick films with B₂O₃–Li₂O glass sintering aid were prepared by the screen printing method on Al₂O₃ substrates. A 200 MPa isostatic pressure was applied to the films before sintering. After being sintered at 950^∘C, lower porosity and denser microstructure was obtained compared with the films without isostatic pressing. The dielectric constant and dielectric loss were 238 and 0.0028, respectively. A tunability of 61.7% was obtained for the isostatic pressed films, a 27.8% enhancement compared to unpressurized films. These results suggest that isostatic pressing …