Open Access. Powered by Scholars. Published by Universities.®
- Discipline
Articles 1 - 5 of 5
Full-Text Articles in Mechanical Engineering
Exploration Of Warm-Up Protocols On Muscular Fatigue, Sahil Kapadia
Exploration Of Warm-Up Protocols On Muscular Fatigue, Sahil Kapadia
Honors Undergraduate Theses
Muscular dystrophy is a genetically linked myopathy with no cure available. The lack of a cure makes early detection and treatment of muscular dystrophy imperative. When reviewing protocols examining muscular fatigue at submaximal isometric contractions, proper warm-up appeared to be absent and could have caused skewed results and conclusions. This study examines the effects of implementing a warm-up protocol before fatiguing trials. In this study, 10 adult subjects conducted fatiguing protocols with the right rectus at submaximal isometric contractions. The warm-up period included a light walk along with contractions at 20% and 33% of maximal voluntary isometric contraction (MVIC) levels. …
Electromyographic And Mechanomyogrpahic Signal Changes With Fatigue In Adults, Rehana Koilpillai
Electromyographic And Mechanomyogrpahic Signal Changes With Fatigue In Adults, Rehana Koilpillai
Honors Undergraduate Theses
Surface electromyography (sEMG) and mechanomyography (MMG) are well-studied signals that can reveal information about the physiological behavior of muscles during contraction. The purpose of this study was to quantify, characterize, and analyze the electrical and mechanical muscle responses to submaximal, isometric contractions in the rectus femoris in adults. Previous studies have investigated the use of EMG to monitor muscle fatigue. However, more information appears to be needed about the use of MMG to measure muscle fatigue during submaximal isometric contraction in the rectus femoris. In this study, the utility of MMG as a measure of muscle fatigue or muscle state …
A Hybrid Constitutive Model For Creep, Fatigue, And Creep-Fatigue Damage, Calvin Stewart
A Hybrid Constitutive Model For Creep, Fatigue, And Creep-Fatigue Damage, Calvin Stewart
Electronic Theses and Dissertations
In the combustion zone of industrial- and aero- gas turbines, thermomechanical fatigue (TMF) is the dominant damage mechanism. Thermomechanical fatigue is a coupling of independent creep, fatigue, and oxidation damage mechanisms that interact and accelerate microstructural degradation. A mixture of intergranular cracking due to creep, transgranular cracking due to fatigue, and surface embrittlement due to oxidation is often observed in gas turbine components removed from service. The current maintenance scheme for gas turbines is to remove components from service when any criteria (elongation, stress-rupture, crack length, etc.) exceed the designed maximum allowable. Experimental, theoretical, and numerical analyses are performed to …
Thermomechanical Fatigue Life Prediction Of Notched 304 Stainless Steel, Justin Karl
Thermomechanical Fatigue Life Prediction Of Notched 304 Stainless Steel, Justin Karl
Electronic Theses and Dissertations
The behavior of materials as they are subjected to combined thermal and mechanical fatigue loads is an area of research that carries great significance in a number of engineering applications. Power generation, petrochemical, and aerospace industries operate machinery with expensive components that undergo repeated applications of force while simultaneously being exposed to variable temperature working fluids. A case of considerable importance is found in steam turbines, which subject blades to cyclic loads from rotation as well as the passing of heated gases. The complex strain and temperature histories from this type of operation, combined with the geometric profile of the …
Creep-Fatigue Crack Initiation And Propagation Of A Notched Stainless Steel, Scott Keller
Creep-Fatigue Crack Initiation And Propagation Of A Notched Stainless Steel, Scott Keller
Electronic Theses and Dissertations
Premature failures of vital gas turbine components, such as blades and vanes, have been the result of increasing demands of power generation facilities. As power needs fluctuate throughout the day, operators are quickly firing up gas turbines as a means of providing instant power. Traditionally, these engines run at constant operating conditions; however, contemporary operating conditions call for these engines to be applied on an “as necessary” basis. The result of the cyclic startup and shutdown of gas turbines has led to a phenomenon known as creep-fatigue (CF). A coupling of two primary failure mechanisms in gas turbines, CF conditions …