Freeze-Form Extrusion Fabrication Of Composite Structures, Ming-Chuan Leu, Lie Tang, Bradley K. Deuser, Robert G. Landers, Greg Hilmas, Shi C. Zhang, Jeremy Lee Watts
Freeze-Form Extrusion Fabrication Of Composite Structures, Ming-Chuan Leu, Lie Tang, Bradley K. Deuser, Robert G. Landers, Greg Hilmas, Shi C. Zhang, Jeremy Lee Watts
Mechanical and Aerospace Engineering Faculty Research & Creative Works
A Freeze-form Extrusion Fabrication (FEF) process capable of making three-dimensional (3D) parts and structures with graded composite materials is presented in this paper. The process development includes the design and manufacture of a gantry machine with a triple-extruder mechanism and the associated electronics hardware and computer software for fabricating functionally graded parts from multiple aqueous pastes. A rheological behavior study with Al2O3 paste is performed to identify an efficient binder for transforming the paste into a pseudoplastic with a high yield stress. A green part is first fabricated using the triple-extruder FEF machine in a layer-by-layer manner …
Effect Of Particle Size, Binder Content And Heat Treatment On Mechanical Properties Of 13-93 Bioactive Glass Scaffolds, Krishna C. R. Kolan, Ming-Chuan Leu, Greg Hilmas, Mariano Garcia Velez
Effect Of Particle Size, Binder Content And Heat Treatment On Mechanical Properties Of 13-93 Bioactive Glass Scaffolds, Krishna C. R. Kolan, Ming-Chuan Leu, Greg Hilmas, Mariano Garcia Velez
Mechanical and Aerospace Engineering Faculty Research & Creative Works
Particle size, binder content and the post-processing schedule are important parameters that affect the microstructure, and, hence, the mechanical properties of parts produced using the indirect selective laser sintering process. 13-93 bioactive glass, with mean particle sizes ranging from 10 μm to 44 μm, is mixed with different amounts of stearic acid binder to fabricate green scaffolds. Through the design of the post-processing schedule, the time required for postprocessing the green scaffolds is reduced from the initial 80 hrs to 12 hrs. The compressive strength varies from 41 MPa for a part with~60% porosity to 157 MPa for a part …