Sputtering Power Effects On Growth And Mechanical Properties Of Cr2alc Max Phase Coatings, Muhammad Naveed, Aleksei Obrosov, Andrzej Zak, Wlodzimierz Dudzinski, Alex A. Volinsky, Sabine Weiß
Sputtering Power Effects On Growth And Mechanical Properties Of Cr2alc Max Phase Coatings, Muhammad Naveed, Aleksei Obrosov, Andrzej Zak, Wlodzimierz Dudzinski, Alex A. Volinsky, Sabine Weiß
Mechanical Engineering Faculty Publications
Coating growth and mechanical properties of nanolamellar Cr2AlC coatings at various sputtering power were investigated in the present study. Cr2AlC coating was deposited on the IN 718 superalloy and (100) Si wafers by DC magnetron sputtering at different sputtering powers. The structure and properties were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and nanoindentation. It was found that coatings had columnar structure with nanocrystalline substructure. Deposition rate increased with the sputtering power. XRD results showed the presence of the Cr2AlC MAX phase, intermetallic AlCr2 and Cr7 …
Modified Yttrium Hydroxide/Mc Nylon Nanocomposites And Scaling Effects In Multilayer Polyethylene Films, Jia Chen
USF Tampa Graduate Theses and Dissertations
In this thesis, monomer casting (MC) nylon was synthesized. MC nylon could replace nonferrous metals in certain applications, including gears, wheels, and other moving parts. However, compared with metals, MC nylon products have poor strength and stiffness, and crack easily, especially at low temperatures. In addition, the dimensional stability of MC nylon is poor, especially in the large casting nylon products, causing significant internal stresses due to shrinkage. Thus, MC nylon cracks easily when cast and molded. The yttrium hydroxide particles were modified by stearic acid and dispersed in the caprolactam. The polymerization time was short due to fast anionic …