Mechanical Engineering Commons^™

Stress Corrosion Cracking And Hydrogen Embrittlement Of Martensitic Alloy Ep-823, Mohammad K. Hossain

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), localized corrosion, and hydrogen embrittlement (HE) susceptibility of martensitic Alloy EP-823 in neutral and acidic solutions at ambient and elevated temperatures. While no failures were observed in smooth specimens in the neutral solution, failures were noticed in the 90°C acidic solution at constant-load (CL) leading to a threshold stress (O'_th) of 102 ksi. The presence of a notch reduced the O'_th value to 91 ksi in a similar environment. The ductility (%El and %RA), time-to-failure (TTF), and true failure stress (O'_r) were gradually …

Environment Assisted Cracking Of Target Structural Materials Under Different Loading Conditions, Venkataramakrishnan Selvaraj

UNLV Theses, Dissertations, Professional Papers, and Capstones

Martensitic Alloy HT-9 has been tested for its evaluation of stress corrosion cracking resistance in neutral and acidic solutions at ambient and elevated temperatures incorporating smooth and notched cylindrical specimens under constant load and slow strain rate (SSR) conditions. C-ring and U-bend specimens have also been tested for stress corrosion cracking evaluation in the acidic solution. The role of hydrogen on the cracking tendency has been evaluated by cathodic applied potential.

The results of constant load testing enabled the determination of the threshold stress for stress corrosion cracking in susceptible environments. The magnitudes of ductility parameters were reduced with increasing …

Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati

UNLV Theses, Dissertations, Professional Papers, and Capstones

The susceptibility of Alloy EP-823 to stress corrosion cracking has been evaluated using smooth and notched cylindrical specimens in neutral and acidic solutions at ambient and elevated temperatures using constant load and slow strain rate testing (SSR) techniques. C-ring and U-bend specimens have also been tested in the acidic solution. The effect of hydrogen on the cracking susceptibility has been evaluated under controlled cathodic potential. While no failures were observed with smooth specimens at constant load, the notched specimens showed failure. The SSR test results indicate that the true failure stress (o'_f), time to failure and ductility parameters …

Embrittlement And Localized Corrosion In Alloy Ht-9, Sudheer Sama

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), hydrogen embrittlement (HE) and localized corrosion susceptibility of Alloy HT -9 in neutral and acidic solutions at 30, 60 and 90°C. Constant-load and slow-strain-rate (SSR) testing techniques were used to evaluate the SCC and HE behavior of this alloy by using smooth and notched tensile specimens. Hydrogen effect on the cracking behavior was evaluated by applying cathodic (negative) potential to the test specimens. Localized corrosion susceptibility was evaluated by cyclic potentiodynamic polarization technique. The results of constant load SCC testing showed a threshold stress at 80% of the …