Oxidation Of Borides And Carbides With Y2o3 And Ta Additions, Salvador Manuel Rodriguez

Open Access Theses & Dissertations

The study presented here describes an investigation of an oxidation scale of a fully-sintered Y2O3-ZrB2-TiC composite exposed in air at 1173K. Upon oxidation of the boride/carbide, a ZrO2-TiO2 was expected to form similar to the ZrO2-SiO2 dual scale of an oxidized ZrB2-SiC. The 47wt% Y2O3-38wt%ZrB2-16wt%TiC composite formed a dual scale consisting primarily of an Y2O3-ZrO2-TiC inner scale with an outer scale of ZrO2-TiO2-Y2O3.

The samples oxidized with a parabolic layer growth allowing the calculation of the effective diffusion coefficient indicating that the oxidation was controlled by oxygen ingress through primarily the ZrO2-Y2O3 phase. The oxygen potential between the inner layer …

Processing Of Zrb2-Zrc-Zrxsiy Ceramic By Reactive Metal Penetration, Nischel B. Maheswaraiah

Open Access Theses & Dissertations

The processing of ZrB2-ZrC-ZrxSiy composite by reactive metal penetration was investigated as a successor to the ZrB2-SiC composites for hypersonic vehicles application, which cannot be used for extended time at temperatures greater than 1600C due to formation of SiO and CO gases. Zirconium (Zr), zirconium disilicide (ZrSi2), and boron carbide (B4C) were reacted in graphite crucibles for 60, 120, 180, and 240 minutes. Microscopy and x-ray diffraction (XRD) deduced the formation of a heterogeneous microstructure of ZrB2-ZrC-ZrxSiy precipitates surrounded by a solidified Zr-Si melt. Unreacted boron carbide was observed in samples held at 1860C for 60 minutes and 120 minutes, …