Embrittlement And Localized Corrosion In Alloy Ht-9, Sudheer Sama

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), hydrogen embrittlement (HE) and localized corrosion susceptibility of Alloy HT -9 in neutral and acidic solutions at 30, 60 and 90°C. Constant-load and slow-strain-rate (SSR) testing techniques were used to evaluate the SCC and HE behavior of this alloy by using smooth and notched tensile specimens. Hydrogen effect on the cracking behavior was evaluated by applying cathodic (negative) potential to the test specimens. Localized corrosion susceptibility was evaluated by cyclic potentiodynamic polarization technique. The results of constant load SCC testing showed a threshold stress at 80% of the …