Development And Use Of A Simple Test Method To Evaluate Reheat Cracking Sensitivity In The Weld Deposit Region Of A Submerged Arc Weld, Maxwell Calder Trent

Masters Theses

Several fabricators have recently noted the occurrence of reheat cracking in the weld deposits of 2¼[ two and one fourth]Cr‑1Mo‑¼[one fourth]V (22V) during the fabrication of pressure vessels used in the petrochemical industry. Due to increased oversight now required during fabrication of already expensive pressure vessels, studies have commenced worldwide in an effort to identify root causes and formulate mitigating actions to weld reheat cracking issues. The Materials Joining Group (MJG) at the University of Tennessee at Knoxville (UTK) have adapted an existing reheat cracking test originally developed for use with alloys similar to 22V. This original C‑Ring test was …