Materials Science and Engineering Commons^™

Recent Progresses In Molybdenum-Based Electrocatalysts For The Hydrogen Evolution Reaction, Ze-Xing Wu, Jie Wang, Jun-Po Guo, Jing Zhu, De-Li Wang

Journal of Electrochemistry

Electrochemical catalytic production of hydrogen has been considered as a promising and sustainable strategy for clean and renewable energy technologies. Molybdenum-based non noble metal catalysts for the hydrogen evolution reaction have attracted extensive attention due to its effective catalytic performance. In this review, the recent progresses in molybdenum-carbide, phosphide, nitride and sulfide electrocatalysts are presented. In addition, the strategies to improve the catalytic performance are analyzed and the prospects for the future development trends are expected.

A Novel Silica-Based Nano Pigment As A Titanium Dioxide Replacement, Ryan Stoneburner

Masters Theses

This research focused on the evaluation of a new Silica-based pigment for the replacement of titanium dioxide (TiO₂) in paperboard coatings. The silica-based pigment has shown the ability to be a replacement in terms of functionality and runnability. TiO₂ is currently the highest opacifying pigment used in paper coatings, but it is also the most costly. Finding a less expensive pigment that doesn't reduce effectiveness is critical to reducing the cost of TiO₂ formulations. To evaluate the new pigment, coatings will be applied using a Cylindrical Laboratory Coater (CLC) with varying amounts of TiO₂ and …

Pulse Electrodeposition Of Pd-Ni Alloy Nanoparticles For Electrocatalytic Oxidation Of Formic Acid, Fang-Zu Yang, Jun-Pei Yue, Zhong-Qun Tian, Shao-Min Zhou

Journal of Electrochemistry

The Pd-Ni alloy nanoparticles with nickel atomic contents of 12.0%, 16.4% and 22.6% were successfully electrodeposited from a Pd-Ni alloy electrolyte by square wave pulse plating. The alloy nanoparticles were in the spherical shape with a diameter of 50 ~ 80 nm. As the growth potential of the alloy was negatively shifted, the nickel content of the alloy was increased, and the size of the nanoparticles was almost the same, whereas the number, the degree of crosslinking and the real active area of the nanoparticles were increased. As the nickel content of the alloy nanoparticles increased, the peak current for …

Controllable Synthesis Of Dispersed Spherical Fe3O4 Nanoparticles As Lithium-Inserted Materials, Hong-Li Zou, Wei-Shan Li

Journal of Electrochemistry

Dispersed spherical Fe₃O₄ nanoparticles were synthesized by a hydrothermal method. The influences of odecyl trimethyl ammonium bromide (DTAB) concentration on the morphology and particle size of the as-prepared Fe₃O₄ were studied. Electrochemical performance of the as-prepared sample as anode materials of lithium ion battery was investigated. It is found that the as-prepared sample exhibits superior rate performance and cycle performance. The nano-sized materials provide structural stability and favor the transfer of lithium ions.

Photoelectrochemical Properties Of Tio_2 Nanoparticles, Jie Qu, Ying Li, Qi-Wei Jiang, Xue-Ping Gao

Journal of Electrochemistry

The protonated titanate nanoparticles were obtained at room temperature and subsequently calcined at different temperatures(300 ℃,400 ℃,500 ℃,600 ℃ and 700 ℃) in air.The obtained products were characterized by XRD,TEM and UV-Vis.It is found that the grain sizes of TiO2 nanoparticles calcined at 300 ℃ were about 20 nm,and increased gradually with the temperature rise.Photoelectric performance was measured with I～V curve and electrochemical impedance spectroscopy(EIS).The TiO2 nanoparticles obtained at 500 ℃ showed the best photoelectrochemical properties with a photovoltaic conversion efficiency of 6.39%,which is much higher than those at other temperatures.In addition,it is also demonstrated that the charge transfer resistance …

Observed Superspin-Glass Behavior In Ni0.5zn0.5fe2o4 Nanoparticles, Antony Adair

Open Access Theses & Dissertations

In this investigation we seek to identify the magnetic behavior of Ni0.5Zn0.5Fe2O4 nanoparticles though AC-susceptibility and DC-magnetization measurements. Powder x-ray diffraction was performed to determine the purity and average diameter ( ~ 9nm) of the particles. Aditionally, structure was confirmed by comparison through the International Centre for Diffraction Data's Powder Diffraction File [52] (PDF # 08-0234).

Zero-field cooled and field cooled DC magnetization measurements (bifurcation and blocking temperature), as well as M(H) hysteresis (below and above the blocking temperature) lead us to initially suggest that the material may in fact be superparamagnetic. However, further investigation of the real AC susceptibility …

Electrodeposition Of Nano-Sb-Zn Alloy In Acetamide-Urea-Nabr-Kbr Melt, Peng Liu, Xin-Ai Guo, Ye-Xiang Tong, Qi-Qin Yang

Journal of Electrochemistry

The electroreduction of Zn(II) and Sb(III) in acetamide-urea-NaBr-KBr(343 K) were studied by cyclic volatmmetry.The reduction of Zn(II) or Sb(III) to the metals is an irreversible process.The transfer coefficient of Zn(II)+2e→Zn and Sb(III) +3e→Sb were calculated to be 0.231 and 0.319,the diffusion coefficient of Zn(II) and Sb(III) in the melt were determined as 1.70 10~(-6) and 3.21 10~(-6) cm~(2)· s~(-1) respectively.The Zn-Sb films with different Zn content from 29.67 at% to 97.34 at% were electrodeposited in acetamide-urea-NaBr-KBr melt at 343 K by controlling the deposition potential and the Zn(II)/Sb(III) molar ratio.The morphology of Zn-Sb film was observed by SEM.Zn-Sb film comprises …