Peridynamic Models For Fatigue And Fracture In Isotropic And In Polycrystalline Materials, Guanfeng Zhang

Department of Mechanical and Materials Engineering: Dissertations, Theses, and Student Research

To improve design and reliability, extensive efforts has been devoted to understanding damage and failure of materials and structures using numerical simulation, as a complement of theory and experiment. In this thesis, peridynamics is adopted to study fatigue and dynamic failure problems.

Fatigue is a major failure mode in engineering structures. Predicting fracture/failure under cyclic loading is a challenging problem. Classical model cannot directly be applied to problems with discontinuities. A peridynamic model is adopted in this work because of important advantages of peridynamics in allowing autonomous crack initiation and propagation. A recently proposed peridynamic fatigue crack model is considered …

Fatigue Properties Of Magnetorheological Elastomers And The Design Of Interfacial Layers To Improve Fatigue Life., Yanfen Zhou

Doctoral

The primary aim of this PhD programme was to understand the fatigue behaviour of magnetorheological elastomers (MREs) and provide a reliable fatigue life predictor for this class of materials. To realise this aim required the study of the dynamic behaviour of MREs using the equi-biaxial bubble inflation test method. Isotropic and anisotropic MREs were fabricated from silicone rubber (SR) filled with soft carbonyl iron (CI) particles. The equi-biaxial fatigue behaviour of these samples was determined using a bubble inflation method. Wöhler (S-N) curves for both isotropic and anisotropic MREs were produced by subjecting the compounds to cycling over a range …