Processing And Composition Effects On The Fracture Behavior Of Spray-Formed 7xxx Series Al Alloys, Mala M. Sharma, Constance W. Ziemian, Timothy J. Eden

Faculty Journal Articles

The fracture properties of high-strength spray-formed Al alloys were investigated, with consideration of the effects of elemental additions such as zinc,manganese, and chromium and the influence of the addition of SiC particulate. Fracture resistance values between 13.6 and 25.6 MPa (m)^1/2 were obtained for the monolithic alloys in the T6 and T7 conditions, respectively. The alloys with SiC particulate compared well and achieved fracture resistance values between 18.7 and 25.6 MPa (m)^1/2. The spray-formed materials exhibited a loss in fracture resistance (KI) compared to ingot metallurgy 7075 alloys but had an improved
performance compared to high-solute powder …