Failure Mechanism Of Woven Roving Fabric/Vinyl Ester Composites In Freeze–Thaw Saline Environment, Elias Anis Toubia, Sadra Emami, Donald A. Klosterman

Civil and Environmental Engineering and Engineering Mechanics Faculty Publications

This experimental study investigates the degradation mechanisms of a glass fiber-reinforced plastic material commonly used in civil engineering applications. A substantial reduction in tensile, shear, and compression properties was observed after 100 days of freeze–thaw cycling in saline environment (-20°C to 20°C). Non-destructive inspection techniques were progressively conducted on unexposed (ambient condition) and exposed (conditioned) specimens. The dynamic mechanical analysis showed permanent decrease in storage modulus that was attributed to physical degradation of the polymer and/or fiber–matrix interface. This indicated the formation of internal cracks inside the exposed glass fiber-reinforced plastic laminate. The 3D X-ray tomography identified preferred damage sites …