Engineering Science and Materials Commons^™

Thermal Shock Studies On Carbon-Carbon Composites: Experimentation And Analysis, Alma Lucia Leanos

Open Access Theses & Dissertations

The oxidation behavior of C/C composites under thermal shock conditions in air is understood and predicted experimentally and by computational efforts. In Chapter. 1, both compressive properties and oxidation behavior of pristine and thermal shock exposed 2D C/C composite specimens were examined. Pristine test specimens were exposed to thermal shock conditions with temperatures ranging from 400°C to 1000°C in an oxidizing environment, followed by compression tests on pristine and thermal shock exposed specimens to obtain their compressive responses.

Similarly, in Chapter. 2, the influence of thermal shock conditions on both, the extent of carbon materials decomposition and the through-thickness compressive …

High Temperature Oxidation Of Nb-Cr-Mo-Si-B Alloys, Kathryn S. Thomas

Open Access Theses & Dissertations

It has been the trend to use nickel based superalloys in high temperature applications, however higher temperatures are required in the effort to enhance the efficiency of such components as jet turbine engines. The melting temperature of the nickel based superalloy limits the extent to which temperature can be raised as these materials are typically used at temperatures within 200 degrees of their melting point. Refractory metal based systems are attractive due to their high melting points, low densities, and good high temperature strength. However, in such cases as niobium, poor oxidation resistance limits the widespread use of such alloys. …