Preparation And Characterization Of The Lani0.6fe0.4o3-Δ Cathode For Intermediate Temperature Solid Oxide Fuel Cell, Hang Liu, Bo Huang, Xin-Jian Zhu

Journal of Electrochemistry

The LaNi0.6Fe0.4O3-δ as cathode material for intermediate temperature solid oxide fuel cell was prepared using a combustion synthesis technique. The X-ray diffraction (XRD) pattern showed that the single-phase LaNi0.6Fe0.4O3-δ perovskite could be obtained after heat treatment at 600°C. The TEM and SEM images of the synthesized powders revealed that the grains were 50-100nm. According to the electrochemical impedance spectra (EIS), the polarization resistance of the symmetric cell LaNi0.6Fe0.4O3-δ/ScSZ/LaNi0.6Fe0.4O3-δ sintered at 1050°C was the smallest (0.70Ω?cm2, 0.27Ω?cm2 and 0.12Ω?cm2 at 750°C, 800°C and 850°C, respectively). In the presence of the Fe-Cr alloy interconnection at 750°C, the cathode performance showed that, with …