Articles 1 - 3 of 3
Full-Text Articles in Engineering Science and Materials
Preparation And Supercapacitive Properties Of Co(Oh)_2/Nay Composite, Chi Ma, Ling-Bin Kong, Yong-Chun Luo, Long Kang
Preparation And Supercapacitive Properties Of Co(Oh)_2/Nay Composite, Chi Ma, Ling-Bin Kong, Yong-Chun Luo, Long Kang
Journal of Electrochemistry
The Co(OH)2/NaY composite was prepared by chemical precipitation method and then tested as an active electrode material for an electrochemical supercapacitor.The results indicated that the composite displayed superior capacitive performance.The maximum specific capacitance of Co(OH)2 was 632.5 F/g.The structure and electrochemical properties of the composite were also discussed.
Molten Salt Treatment Of Mno_2 And Investigation On Supercapacitor Properties, Ye Chen, Zun-Bo Zhang, Wei Zhang, Liang Liu, Zhi-Min Liu
Molten Salt Treatment Of Mno_2 And Investigation On Supercapacitor Properties, Ye Chen, Zun-Bo Zhang, Wei Zhang, Liang Liu, Zhi-Min Liu
Journal of Electrochemistry
The MnO2 prepared by solid phase method is treated by KCl-NaCl-LiCl molten salt system.The XRD patterns indicated that the crystal structures of MnO2 sample have had the α-MnO2 and γ-MnO2 phase,the crystallinity of sample is increased after treated by molten salt.The electrochemical properties were tested by cyclic voltammetry,constant current charge/discharge and AC impedance.The result shows that the supercapacitor performance of the treated material has improved.The specific discharge capacitance of the treated sample are 129.07 F·g-1,increased by 27.88% compared to 100.94 F·g-1 of untreated sample.Long cycle life and high coulombic efficiency were also demonstrated after charge/discharge 100 cycles.The value of RESR …
A Study On Supercapacitor Based On Aligned Carbon Nanotubes, Xiao-Yan Ye, Yan-Zhi Wang, Hai-Yan Song, Zhuo Sun, Pin-Gang He, Yu-Zhi Fang
A Study On Supercapacitor Based On Aligned Carbon Nanotubes, Xiao-Yan Ye, Yan-Zhi Wang, Hai-Yan Song, Zhuo Sun, Pin-Gang He, Yu-Zhi Fang
Journal of Electrochemistry
Large scale vertically aligned carbon nanotubes(ACNTs) with uniform length and diameter were prepared by the pyrolysis of iron(Ⅱ) phthalocyanine at low pressure.The ACNTs were activated by electrolyte-activation,acid-activation or electrochemical activation.The performance of the capacitor based on activated ACNTs was characterized by cyclic voltammograms which was of rectangular shape,impedence spectroscopy in which the phase is above 80° and the result specific capacitance was 16～32 F/g,which suggest that the ACNTs are the promising material for the supercapacitor.