The Effects Of Microstructure On Fretting Fatigue Behavior Of Nickel Alloy In-100, Erik C. Saladin

Theses and Dissertations

This thesis studied the effect of microstructure on the fretting fatigue behavior of IN-100. First, fretting and plain fatigue S-N curves were determined over a large range of applied stress at an identical R-ratio and for fretting tests, done with a constant contact load. It was found that fretting fatigue reduces the cycles to failure compared to plain fatigue. The half contact width was found for the specimens, the crack initiation angle was found to be 40 deg and the crack initiation location was at the trailing edge of contact for the fretting specimens. Computational work included finding the stress …