Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Under Strain Controlled Tension-Tension And Tension-Compression Loading, James J. Gudaitis
Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Under Strain Controlled Tension-Tension And Tension-Compression Loading, James J. Gudaitis
Theses and Dissertations
This stuidy investigates the fatigue response of a cross-ply [0/90]2s Nicalon/Calcium Aluminosillicate (Nicalcc/CAS) ceramic matrix composite at room temperature under strain controlled tension-tension and tension-compression fatigue loading. The primary objectives were to determine strain fatigue limits for both loading cases and to complete a fatigue life diagram (Δe-N) for all tests. Failure mechanisms were also studied. The average initial modulus value for this lay-up was 120 GPa. The ultimate tensile strain was 0.00988 mn/mm (285 MPa). Eight tests were conducted with maximum strains that ranged from 0.00300 mm/mm to 0.00722 mm/mm. The tension-tension fatigue limit was found to be …
Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite At Elevated Temperatures Under Tension-Tension Loading, Richard J. Tuznik
Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite At Elevated Temperatures Under Tension-Tension Loading, Richard J. Tuznik
Theses and Dissertations
A study was conducted which investigated the behavior of a Nicalon/ Calcium-Aluminosilicate (Nicalon/CAS) cross-ply [0/90]2S ceramic matrix composite at elevated temperatures under tension-tension fatigue loading. Tension-tension fatigue tests were performed with a load ratio of R = 0.10 and a frequency of 10 Hertz at 700°C and 850°C. These results were compared to results from a previous study conducted at room temperature. Material behavior and damage was recorded by fatigue life curves, elastic modulus' maximum and minimum strain, acetate replication techniques, and post-mortem fractography. Analysis of these results showed identical matrix dominated damage behavior at RT and 700°C. Ultimate …