Articles 1 - 2 of 2
Full-Text Articles in Engineering Science and Materials
Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati
Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati
UNLV Theses, Dissertations, Professional Papers, and Capstones
The susceptibility of Alloy EP-823 to stress corrosion cracking has been evaluated using smooth and notched cylindrical specimens in neutral and acidic solutions at ambient and elevated temperatures using constant load and slow strain rate testing (SSR) techniques. C-ring and U-bend specimens have also been tested in the acidic solution. The effect of hydrogen on the cracking susceptibility has been evaluated under controlled cathodic potential. While no failures were observed with smooth specimens at constant load, the notched specimens showed failure. The SSR test results indicate that the true failure stress (o'f), time to failure and ductility parameters …
Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran
Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran
UNLV Theses, Dissertations, Professional Papers, and Capstones
This investigation is focused on the evaluation of stress corrosion cracking (SCC) and localized corrosion behavior of Type 422 stainless steel in aqueous environments at ambient and elevated temperature. The results of constant load SCC testing using smooth specimens showed no failure in the neutral solution but a threshold stress of 97 ksi was observed in the 90°C acidic environment. SCC testing by the slow-strain-rate test method indicate that the time-to-failure, true failure stress and ductility parameters were gradually reduced with increasing temperature, showing more pronounced effect in the acidic solution. The application of a controlled cathodic potential showed further …