Wear Analysis Of Cu-Al Coating On Ti-6al-4v Under Fretting, Karl N. Murray
Wear Analysis Of Cu-Al Coating On Ti-6al-4v Under Fretting, Karl N. Murray
Theses and Dissertations
The effects of changes in the coefficient of friction (CoF) between the contacting surfaces on the fretting wear characteristics of Cu-Al coating on Ti-6Al-4V were investigated. This Cu-Al coating is part of a system that is applied to titanium turbine blades to reduce fretting at the interface. In the application, there is a solid lubricant that is added on top of the coating as an assembly aid and to help reduce the friction while the lubricant remains within the contact. Previous studies have researched the characteristics of the coating without the additional lubricant. In this study, liquid motor oil was …
Effects Of Shot-Peening On High Cycle Fretting Fatigue Behavior Of Ti-6al-4v, Halil I. Yuksel
Effects Of Shot-Peening On High Cycle Fretting Fatigue Behavior Of Ti-6al-4v, Halil I. Yuksel
Theses and Dissertations
Effects of Shot-peening on High Cycle Fretting Fatigue behavior of Ti-6Al-4V were investigated. Experiments were performed with 6.35 mm thick specimens which provided S/N curves. After the tests, it was observed that the specimens failed near the trailing edge of contact. Scanning Electron Microscopy showed that cracks initiated on the contact surface for 6.35 mm, and at the depth of specimen ranging from 200 to 300 microns for 3.81 mm thick specimens. Initial crack orientation was around 37 and 42 degrees respectively for 6.35 and 3.81 mm thicknesses. Finite Element Analysis (FEA) was conducted, and using FEA results, Smith-Watson-Topper, Findley, …