Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Under Strain Controlled Tension-Tension And Tension-Compression Loading, James J. Gudaitis
Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Under Strain Controlled Tension-Tension And Tension-Compression Loading, James J. Gudaitis
Theses and Dissertations
This stuidy investigates the fatigue response of a cross-ply [0/90]2s Nicalon/Calcium Aluminosillicate (Nicalcc/CAS) ceramic matrix composite at room temperature under strain controlled tension-tension and tension-compression fatigue loading. The primary objectives were to determine strain fatigue limits for both loading cases and to complete a fatigue life diagram (Δe-N) for all tests. Failure mechanisms were also studied. The average initial modulus value for this lay-up was 120 GPa. The ultimate tensile strain was 0.00988 mn/mm (285 MPa). Eight tests were conducted with maximum strains that ranged from 0.00300 mm/mm to 0.00722 mm/mm. The tension-tension fatigue limit was found to be …