The High Temperature Corrosion Of 2205 Duplex Stainless Steel With Nacl Deposit, Fu-Fu Peng, Chaur-Jeng Wang, Yu-Chang Lin

Journal of Electrochemistry

The objective of this study was to figure out the hot corrosion behavior of 2205 duplex stainless steel(2205 DSS) within the temperature ranges from 550 to 850℃ in the static air condition with 2 mg/cm~(2)NaCl deposit,and in the air atmosphere condition with a constant flow rate of 500 vppm NaCl_((g)),respectively.Experimental results show that the hot corrosion kinetics met the parabolic rate law and the corrosion rate increased constantly with increasing temperature.The scales formed included Fe_(2)O_(3)/Fe_(3)O_(4)/Cr_(2)O_(3) and FeCr_(2)O_(4)from outer layer to inner layer.The sequence of formation is independent of the environment temperature,but the SiO_2 and NiO can be found in the …