The Evaluation Of The Damping Characteristics Of A Hard Coating On Titanium, Christopher M. Blackwell Mar 2004

The Evaluation Of The Damping Characteristics Of A Hard Coating On Titanium, Christopher M. Blackwell

Theses and Dissertations

Engine failures due to fatigue have cost the Air Force an estimated $400 million dollars per year over the past two decades (Garrison, 2001). Damping treatments capable of reducing the internal stresses of fan and turbine blades to levels where fatigue is less likely to occur have the potential for reducing cost while enhancing reliability. This research evaluates the damping characteristics of magnesium aluminate spinel, MgO+Al2O3, (mag spinel) on titanium plates. The material and aspect ratio were chosen to approximate the low aspect ratio blades found in military gas turbine fans. The plates were tested with …


Investigation Of Tension-Compression Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Room And Elevated Temperatures, Elizabeth A. Boyum Dec 1993

Investigation Of Tension-Compression Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Room And Elevated Temperatures, Elizabeth A. Boyum

Theses and Dissertations

This research, the first load-controlled tension-compression fatigue testing to be performed on a MMC, extends the existing knowledge of MMC fatigue damage mechanisms to include the tension compression loading condition. To accomplish this, a (0/90)2, SCS-6/Ti-15-3 laminate was subjected to tension- tension fatigue at room temperature, and tension-compression fatigue at both room temperature and 427°C. Stress and strain data was taken to evaluate the macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanic level. On a maximum applied stress basis, the room temperature tension-tension specimens had longer fatigue lives than the room …