Effects Of Polishing Shot-Peened Surfaces On Fretting Fatigue Behavior Of Ti-6al-4v, Kasey S. Scheel
Effects Of Polishing Shot-Peened Surfaces On Fretting Fatigue Behavior Of Ti-6al-4v, Kasey S. Scheel
Theses and Dissertations
The research of this thesis was done to investigate the effects of polishing a shot-peened specimen of Ti-6Al-4V on the fretting fatigue life of that specimen. The shot-peening process, though one of the most beneficial techniques in prolonging fretting fatigue life, creates a textured surface that may lead to problems on the micro level. This research was done in an attempt to further improve the peening process by examining the effects of another surface treatment to be used in conjunction, surface polishing. The rough peened surface may contain abrupt changes in surface geometry that act as stress risers, which are …
Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle
Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle
Theses and Dissertations
Stress rupture tests on the SylramicTM fiber with an in-situ layer of boron nitride, boron nitride interphase, and SiC matrix ceramic matrix composite were performed at 550°C and 750°C with 0.0, 0.2, or 0.6 atm partial pressure of water vapor, pH2O. The 550°C, 100-hr strengths were 75%, 65% and 51% of the monotonic room temperature tensile strength, respectively. At 750°C, the strengths were 67%, 51%, and 49%, respectively. Field Emission Scanning Electron Microscopy analysis estimated the total embrittlement times for 550°C with 0.0, 0.2, and 0.6 atm pH2O were >63 hrs, >38 hrs, and between …