Experimental Investigation Of Mechanical Behavior Of An Oxide/Oxide Ceramic Composite In Interlaminar Shear And Under Combined Tension-Torsion Loading, Skyler R. Hilburn

Theses and Dissertations

Creep behavior in interlaminar shear of an oxide-oxide ceramic composite, Nextel 720™/aluminosilicate (N720/AS), was investigated at 1100°C in laboratory air and in steam. The interlaminar shear strength (ILSS) was determined as 7.65 MPa. The creep behavior was examined for interlaminar shear stresses in the 2-6 MPa range. Primary and secondary creep regimes were observed in all tests conducted in air and in steam. Tertiary creep was noted in the tests performed at 6 MPa. Larger creep strains and higher creep strain rates were produced in steam. Surprisingly, the presence of steam had a beneficial effect on creep lifetimes. It appears …