Significant Friction Reduction Of High-Intensity Pulsed Ion Beam Irradiated Wc-Ni Against Graphite Under Water Lubrication, Gaolong Zhang, Yuechang Wang, Ying Liu, Xiangfeng Liu, Yuming Wang

Friction

Two types of commercial WC-Ni samples were irradiated with the High-intensity pulsed ion beam (HIPIB). Both the surface characteristics and tribo-characteristics of the non-irradiated and irradiated WC-Ni samples, sliding against graphite under water lubrication, were compared. Quite low steady friction coefficients (approximately of 0.02) of the irradiated WC-Ni were observed. The surface topographies and components were investigated. The quite low friction of the irradiated WC-Ni samples was ascribed to the higher fluid retention capability of the latter and the tribofilm formed during sliding.