The High Temperature Corrosion Of 2205 Duplex Stainless Steel With Nacl Deposit, Fu-Fu Peng, Chaur-Jeng Wang, Yu-Chang Lin
The High Temperature Corrosion Of 2205 Duplex Stainless Steel With Nacl Deposit, Fu-Fu Peng, Chaur-Jeng Wang, Yu-Chang Lin
Journal of Electrochemistry
The objective of this study was to figure out the hot corrosion behavior of 2205 duplex stainless steel(2205 DSS) within the temperature ranges from 550 to 850℃ in the static air condition with 2 mg/cm~(2)NaCl deposit,and in the air atmosphere condition with a constant flow rate of 500 vppm NaCl_((g)),respectively.Experimental results show that the hot corrosion kinetics met the parabolic rate law and the corrosion rate increased constantly with increasing temperature.The scales formed included Fe_(2)O_(3)/Fe_(3)O_(4)/Cr_(2)O_(3) and FeCr_(2)O_(4)from outer layer to inner layer.The sequence of formation is independent of the environment temperature,but the SiO_2 and NiO can be found in the …
Corrosion Fatigue And Dynamic Strain Aging Of Duplex Stainless Steel In Aqueous Solution, Chuan-Ming Tseng, I-Hsuang Lo, Wen-Ta Tsai
Corrosion Fatigue And Dynamic Strain Aging Of Duplex Stainless Steel In Aqueous Solution, Chuan-Ming Tseng, I-Hsuang Lo, Wen-Ta Tsai
Journal of Electrochemistry
The corrosion fatigue and dynamic strain aging behaviors of 22%Cr duplex stainless steel (DSS) in sodium chloride solutions were investigated. Austenitic 316L SS and ferrtic 430 SS were also used in this study for a comparison. The experimental results showed that no stress corrosion cracking (SCC) occurred in all these SSs tested in 3.5wt% NaCl solution at 80 ℃. However, dynamic strain aging (DSA) occurred in 316L austenitic SS and 22%Cr DSS during slow strain rate testing (SSRT) in this solution.The occurrence of DSA was dependent on solution temperature,strain rate and the presence of austenitic phase. The corrosion rate of …
Effects Of Nickel Content And Simulated Heat Affected Zone Of 2205 Duplex Stainless Steel On Pitting Corrosion, Horngyih Liou, Jutung Lee, Wenta Tsai
Effects Of Nickel Content And Simulated Heat Affected Zone Of 2205 Duplex Stainless Steel On Pitting Corrosion, Horngyih Liou, Jutung Lee, Wenta Tsai
Journal of Electrochemistry
The effects of nickel content and Gleeble simulated heat affected zone(HAZ) of 2205 stainless steel on pitting corrosion were investigated in this paper. The results showed that nickel content, ranging from 4.5 wt% to 6.5 wt% in base metal, had only a minor effect on the electrochemical polarization curves, with all Enp's and Epp's falling in the rang of 1 1001200 mV. Comparing with the base metal, the simulated HAZ microstructure caused an increase in the anodic current density, a distinct decrease in both Enp and Epp , and a reduction in the passive range. Furthermore, hysteresis behavior was found …