High Temperature Corrosion Of Aluminized Aisi 4130 Steel With The Different Composition Of Nacl/Na2so4 Deposits, Mohammad Badaruddin, Chaur Jeng Wang, Yudhistyra Saputra, Abu Khalid Rivai
High Temperature Corrosion Of Aluminized Aisi 4130 Steel With The Different Composition Of Nacl/Na2so4 Deposits, Mohammad Badaruddin, Chaur Jeng Wang, Yudhistyra Saputra, Abu Khalid Rivai
Makara Journal of Technology
The high temperature corrosion of AISI 4130 steel can be increased by hot-dip aluminizing coating. The aluminized steel specimens with the deposit composition of 100/0, 30/70, 50/50, 70/30, and 0/100 (wt.%) NaCl/Na2SO4 were oxidized at 750 °C for 1-49 h periods. According to a parabolic rate constant (kp) value, the aluminized steel with deposit composition of 70/30 NaCl/Na2SO4 shows the highest kp value (3.71 × 10-11 g2cm- 4s-1), later followed by the kp value of 3.35 × 10-11 g2cm-4s-1 for 100/0 and the lowest kp value is 7.731 × 10-12 g2cm-4s-1 for 0/100. Whereas, the kp value for the aluminized …
Improvement Of High Temperature Oxidation Of Low Carbon Steel Exposed To Ethanol Combustion Product At 700 °C By Hot-Dip Aluminizing Coating, Mohammad Badaruddin
Improvement Of High Temperature Oxidation Of Low Carbon Steel Exposed To Ethanol Combustion Product At 700 °C By Hot-Dip Aluminizing Coating, Mohammad Badaruddin
Makara Journal of Technology
Low carbon steel (AISI 1005) was coated by hot-dipping into a molten Al-10% Si bath at 700 °C for 18s. After hotdipping treatment, the coating layers consisted of Al, Si, FeAl3, τ5-Fe2Al8Si, and Fe2Al5. The bare steel and the aluminized steel were isothermally oxidized at 700 °C in ethanol combustion product at atmospheric pressure for 49 h. The aluminized steel shows good performance in high temperature oxidation because the formation of Al2O3 layer on the coating surface. The growth of iron oxide nodules on the surface coating was accelerated by rapid outward diffusion of Fe-ions due to the presence of …