Civil and Environmental Engineering Commons^™

Evaluation Of Reducing Cement Content In Ndor Class R Combined Aggregate Gradations, Miras Mamirov, Jiong Hu, Yong-Rak Kim

Nebraska Department of Transportation: Research Reports

The main objective of this research project was to achieve a cement reduction on Nebraska slip-form pavement concrete through aggregate particle packing optimization. A literature review was conducted to examine different aggregate optimization tools, quality control tests, and historical data of Nebraska Department of Transportation (NDOT) pavement mixtures. It was found that the Modified Toufar Model has good potential in optimizing particle packing and predicting packing degrees. The combined aggregate void content test was found to be useful to experimentally justify optimized aggregate gradations. The Box Test with a modified index and image analysis tool for surface void estimation was …

Long-Term Performance Evaluation Of Nudeck In Kearney East Bypass, George Morcous, Marc Maguire

Nebraska Department of Transportation: Research Reports

The Kearney East Bypass bridge is the first project that implements the newly developed precast concrete deck system (known as 2nd generation NUDECK). The new system consists of full-depth full-width precast prestressed concrete deck panels that are 12 ft (3.66 m) long each. The panels have covered shear pockets at 4 ft (1.22 m) spacing on each girder line to host clustered shear connectors that are adjustable in height. Narrow unreinforced transverse joints are used to eliminate the need for deck overlay. Also, deck panels are post-tensioned in the longitudinal direction using a new post-tensioning system that eliminates the need …

Development Of A Mix Design Adjustment Method For Fiber Reinforced Concrete And Super High Performance Concrete Based On Excess Paste, Joe Malloy

Department of Civil and Environmental Engineering: Dissertations, Theses, and Student Research

The main objective of this study was to develop a mix design adjustment method for Fiber Reinforced Concrete (FRC) that would maintain appropriate workability while improving hardened concrete performance. A literature review was conducted to examine existing methods for adjusting mix designs to account for fiber introduction. It was found that while increasing fine aggregate and cement paste content can make up for lost workability with the addition of fibers, no rational mix design adjustment method is available. Reference mix designs from the Nevada Department of Transportation and the Nebraska Department of Transportation were used, and this study focused on …

Evaluation Of Internally Cured Bridge Deck Concrete With Standard And Optimized Aggregate Gradation, Arman Abdigaliyev

Department of Civil and Environmental Engineering: Dissertations, Theses, and Student Research

Due to the relatively high cement content and low water-to-cement ratio (w/c) used, bridge deck concrete is prone to premature cracking. Internal curing has been found to greatly reduce the chance of premature cracking as well as concrete deterioration. This research developed internally cured bridge deck concrete based on a local mix design in Nebraska. Four different lightweight fine aggregate (LWFA) as internal curing agents were evaluated and their effects on fresh, mechanical, durability, and shrinkage properties of concrete were studied. The study focused on resolving two issues associated with fine aggregate replacement based on Bentz equation. To identify the …

Evaluation Of Nebraska’S Aggregate Reactivity By The Miniature Concrete Prism Test Method – Aashto T380, Lieska Halsey, Wally Heyen

Nebraska Department of Transportation: Research Reports

The evaluation of nine different aggregates shows the viability of the T380 test method as an alternative to the standard C1293 test method. The T380 assesses the Alkali-Silica Reaction potential of aggregates with the same reliability as C1293 and correlates well with the C1293 test method. Results are obtained within 56 days by T380 compared to 365 days required by C1293. The T380 method at 56 days appears to characterize the aggregate reactivity similarly to C1293 for all the aggregates evaluated in this study. Therefore, T380 will be part of the Department test method for approval of interground/blended cements along …

Effect Of Moisture Condition On Concrete Core Strengths, Wally Heyen, Lieska Halsey

Nebraska Department of Transportation: Research Reports

The main purpose of this study was to determine if there would be any major differences between curing methods of cores taken for acceptance testing from a highway slab on a project. The comparison provided data to determine the effect of the moisture gradients created by these different curing treatments on core strength and core permeability. The strengths were measured of moist cured cores and sealed plastic bag cured cores from the day cores were obtained (14, 21 and 26 days) until they reached 28 days. Permeability was also measured at 26, 28 and 32 days. According to ASTM C42, …

Investigating The Interaction Of Ndot Hot-Pour Pcc Joint Sealant And Penetrating Concrete Sealers, Bruce Barrett, Dale Byre, Wally Heyen, Lieska Halsey, David Hansen

Nebraska Department of Transportation: Research Reports

Based on the field observations on NE-83, PCS potentially impacts the bond between the concrete and hot-pour sealant after application. If penetrating sealers break the interfacial bond after application, concrete pavements could become compromised and subject to freeze-thaw damage, chloride attack, and other deleterious effects.

The results show that discoloration occurred when applying the five PCS products to the NE-3405 hot-pour sealed testing blocks. All three test methods of application; spraying, 1-min, and 5-min soaks, caused discoloration. The level of discoloration increased with the duration of contact with the PCS. Despite discoloration, none of the five PCS products caused de-bonding …