Mechanical Properties Of Dendritic Pd-Cu-Ga Dental Alloys, Efstratios Papazoglou, Qiang Wu, William A. Brantley, John C. Mitchell, Glyn Meyrick
Mechanical Properties Of Dendritic Pd-Cu-Ga Dental Alloys, Efstratios Papazoglou, Qiang Wu, William A. Brantley, John C. Mitchell, Glyn Meyrick
Cells and Materials
Three Pd-Cu-Ga dental alloys with very similar nominal compositions and dendritic as-cast microstructures were selected for study: Option (Ney Dental) and Spartan (Williams/lvoclar) contain a small amount of boron, while Spartan Plus (Williams/Ivoclar) is boron-free. Bars of each alloy were tested in tension for the as-cast and simulated porcelain-firing conditions, and values of mechanical properties were measured. Fracture surfaces and microstructures of axially sectioned and etched fracture specimens were observed with the scanning electron microscope (SEM). Except for the elastic modulus, significant differences were typically found in alloy properties. Heat treatment eliminated the dendritic microstructure, decreased strength and increased ductility. …
Metallurgical Structures Of As-Cast And Heat-Treated High-Palladium Dental Alloys, William A. Brantley, Zhuo Cai, Alan B. Carr, John C. Mitchell
Metallurgical Structures Of As-Cast And Heat-Treated High-Palladium Dental Alloys, William A. Brantley, Zhuo Cai, Alan B. Carr, John C. Mitchell
Cells and Materials
Scanning electron microscope observations and energy-dispersive spectroscopic analyses have been performed on two first-generation and two second-generation high-palladium dental casting alloys. A specimen design simulating a maxillary central incisor coping was employed to conserve metal, while providing thin and thick sections to yield a range of solidification rates. The alloys were centrifugally cast in air, following standard dental laboratory techniques; three castings were prepared for each alloy. Each casting was sectioned to produce two mirror-image specimens, and one specimen received the appropriate oxidation heat treatment, followed by a simulated full porcelain firing sequence. After metallographic polishing, specimens were examined with …