Full-Text Articles in Aerospace Engineering
Fretting Fatigue Behavior Of Shot-Peened Titanium Alloy Tl-6al-4v Under Seawater Conditions, William Y. Allen
Fretting Fatigue Behavior Of Shot-Peened Titanium Alloy Tl-6al-4v Under Seawater Conditions, William Y. Allen
Theses and Dissertations
The fretting fatigue behavior of the shot-peened titanium alloy, Ti-6Al-4V, was investigated under a corrosive environment of synthetic seawater. Fretting fatigue tests were performed over a wide stress range to determine the effect of seawater at high and low cycle fatigue regimes. The results from this study showed: (1) seawater significantly reduces the fretting fatigue life of shot-peened Ti-6Al-4V at both high and low cycle fatigue relative to its counterpart in ambient laboratory conditions, (2) shot peening increases the fretting fatigue life of Ti-6Al-4V when tested under dry and seawater conditions relative to its counterpart of unpeened Ti-6Al-4V, (3) surface …
Effect Of A Variable Contact Load On Fretting Fatigue Behavior Of Ti-6al-4v, Andrew J. Jutte
Effect Of A Variable Contact Load On Fretting Fatigue Behavior Of Ti-6al-4v, Andrew J. Jutte
Theses and Dissertations
Effects of a variable contact load on the high cycle fretting fatigue behavior of Ti-6AL-4V were investigated. Experimental tests were performed using a new test setup capable of applying a contact load varying in amplitude, frequency, and phase and independently measuring shear forces on opposite sides of a specimen. Finite element analysis (FEA) of experimental and idealized loading conditions was performed and local mechanistic parameters and the Modified Shear Stress Range (MSSR) fatigue parameter were determined. Correlations between contact width, slip amplitude, fatigue life and a variable contact load were established with variable contact loading shown to have a damaging …