Preparation And Low-Temperature Sintering Of Cu Nanoparticles For High-Power Devices
Preparation And Low-Temperature Sintering Of Cu Nanoparticles For High-Power Devices
A.S. Md Abdul Haseeb
One of the fundamental requirements for high-temperature electronic packaging is reliable silicon attach with low and stable electrical resistance. This paper presents a study conducted on Cu nanoparticles as an alternative lead-free interconnect material for high-temperature applications. Cu nanoparticles were prepared using pulsed wire evaporation technique in water medium. Pure Cu nanoparticles without any organic mixture were used in this paper. An economical approach to extract the nanoparticles from water was established. In situ Cu nanoparticles oxide reduction was successfully done using forming gas $({\rm N}-{2}{\hbox{-}}5\%{\rm H}-{2})$. Cross-section analysis on bonded interface shows onset of Cu nanoparticles sintering at 400$^{\circ}{\rm …
Effect Of Temperature On Tribological Properties Of Palm Biodiesel
Effect Of Temperature On Tribological Properties Of Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel, as an alternative fuel is steadily gaining attention to replace petroleum diesel partially or completely. The tribological performance of biodiesel is crucial for its application in automobiles. In the present study, effect of temperature on the tribological performance of palm biodiesel was investigated by using four ball wear machine. Tests were conducted at temperatures 30, 45, 60 and 75 °C, under a normal load of 40 kg for 1 h at speed 1200 rpm. For each temperature, the tribological properties of petroleum diesel (B0) and three biodiesel blends like B10, B20, B50 were investigated and compared. During the wear …
A Technical Note On The Production Of Zirconia And Zircon Brick From Locally Available Zircon In Bangladesh
A.S. Md Abdul Haseeb
In this study, the potentiality of Bangladesh zircon as a raw material for zirconia and zircon brick production was examined. Decomposition of zircon (ZrSiO4) into zirconia (ZrO2) was attempted by using caustic soda (NaOH) as the decomposition agent. 5-10 μm size zircon, 5-30 wt.% NaOH, and decomposition temperatures ranging from 1300 to 1500°C were investigated. X-ray diffraction method using Mo Kα radiation was used in order to find out the extent of decomposition of zircon into zirconia. Zircon bricks of 0.06 mm× 0.06 mm× 0.025 mm shaped were made under a pressure of 15 MPa. Carboxi methyal cellulose (CMC) and …