Engineering Commons^™

Development Of Battery Materials To Function As Corrosion Protection On Car Body Plates, Tubagus Noor Rohmannudin, Sulistijono Sulistijono, Noval Adrinanda, Faridz Wira Dharma, Samuel Areliano

Journal of Materials Exploration and Findings

Most car bodies made for mass production are made from steel or aluminum. Both are strong metals, but steel is cheaper than aluminum and is more commonly used in lower-end cars for a broader consumer range. The weakness of steel compared to aluminum is that it is susceptible to corrosion under certain conditions, and thus it may deteriorate over time without proper care. To prevent corrosion, modern cars are coated with paint to prevent direct contact with the environment. As a second line of protection, a car battery can be connected to the body to create an impressed current cathodic …

Electrochemical Detection For The Corrosion Of Reinforcing Steel In Concrete During Immersion And Drying Cycles, Bing-Li Jia, Fa-He Cao, An-Na Chen, Jian-Qing Zhang

Journal of Electrochemistry

The corrosion behavior of reinforcing steel in concrete under dry-wet cycle condition has been studied by electrochemical noise(EN) compared with the electrochemical impedance spectroscopy(EIS),SEM micrographs and EDS.The statistical method has been employed to analyze the EN data of reinforcing steel in concrete,which revealed three different corrosion stages of reinforcing steel in concrete,including the dissolution of the passive film,the active corrosion and the cumulation of corrosion product.The wavelet transform has also been employed,which indicated that steel in concrete with pH 1 is associated with uniform corrosion,while steel in concrete with pH 3 and pH 7 are associated with localized corrosion,such as …

Corrosion Of Steel In Sea-Bottom Mud Of Nothern China Sea Area, Gong-Yu Guo, Jing-Lei Zhang, Bao-Rong Hou, Fang-Ying Yang

Journal of Electrochemistry

Corrosion experiments of A 3, 16Mn, 20 # as well as ZCE36_225 steel were carried out in southern Bohai sea and Qingdao sea areas. The sea_bottom mud in southern Bohai sea area is the sandy mud and that in Qingdao sea area is pure beach sand. In this experiment, the compareing test of two modes with electric connected and non_electric connected modes was carried out. The experiment results showed that: 1) the corrosion rate of steel in sea_bottom mud has a strong relation with mud types. The corrosion rates of steels in pure beach sand are much higher than those …

Characterization Of Iron Oxides And Atmospheric Corrosion Of Steel, Sei Jin Oh

Physics Theses & Dissertations

The study of corrosion behavior was performed using three different analytical techniques, which provided information on the formation, development and layering of iron oxides on the corrosion products as a function of atmospheric conditions, exposure time and type of steel. In particular, the protective layer formed on weathering steel was investigated as a function of different amounts of alloying elements in the steel, atmospheric conditions and exposure times. Combined together, the results provided a better understanding of the atmospheric corrosion behavior of steel, and formed a part of database of the atmospheric corrosion characteristics.

Accurate characterization of the iron oxides …