Articles 1 - 5 of 5
Full-Text Articles in Engineering
Magnetic Resonance Imaging Analysis Of Molecular Mobility During Dissolution Of Poly(Vinyl Alcohol) In Water, Balaji Narasimhan, J. E.M. Snaar, R. W. Bowtell, S. Morgan, C. D. Melia, N. A. Peppas
Magnetic Resonance Imaging Analysis Of Molecular Mobility During Dissolution Of Poly(Vinyl Alcohol) In Water, Balaji Narasimhan, J. E.M. Snaar, R. W. Bowtell, S. Morgan, C. D. Melia, N. A. Peppas
Balaji Narasimhan
Magnetic resonance imaging is used to study changing microstructure and molecular motion during dissolution of poly(vinyl alcohol) (PVA) in water. One-dimensional water concentration profiles were measured as a function of distance from the polymer-solvent interface. Diffusion-weighted profiles were used to calculate the spatial variation of the self-diffusion coefficient of water. The results indicate that diffusion coefficient values decrease toward the glassy core of the polymer. Self-diffusion coefficient values within the dissolving polymer increase with increasing dissolution time, while those near the polymer-solvent interface remain fairly constant. The effect of PVA molecular weight on the dissolution mechanism was investigated, with MÌ„n …
High Breakdown Strength, Multilayer Ceramics For Compact Pulsed Power Applications, Wayne Huebner, Brian L. Gilmore, Shi C. Zhang, Mike L. Krogh, B. C. Schultz, R. C. Pate, L. F. Rinehart, J. M. Lundstrom
High Breakdown Strength, Multilayer Ceramics For Compact Pulsed Power Applications, Wayne Huebner, Brian L. Gilmore, Shi C. Zhang, Mike L. Krogh, B. C. Schultz, R. C. Pate, L. F. Rinehart, J. M. Lundstrom
Materials Science and Engineering Faculty Research & Creative Works
Advanced ceramics are being developed for use in large area, high voltage devices in order to achieve high specific energy densities (greater than 10^6/ J/m^3/) and physical size reduction. Initial materials based on slip cast TiO2 exhibited a high bulk breakdown strength (BDS greater than 300 kV/cm) and high permittivity with low dispersion (epsilon approximately equal to 100). However, strong area and thickness dependencies were noted. To increase the BDS, multilayer dielectric compositions are being developed based on glass/TiO2 composites. The addition of glass increases the density (approximately equal to 99.8% theoretical), forms a continuous grain boundary phase, and also …
Mechanical Properties Of Dendritic Pd-Cu-Ga Dental Alloys, Efstratios Papazoglou, Qiang Wu, William A. Brantley, John C. Mitchell, Glyn Meyrick
Mechanical Properties Of Dendritic Pd-Cu-Ga Dental Alloys, Efstratios Papazoglou, Qiang Wu, William A. Brantley, John C. Mitchell, Glyn Meyrick
Cells and Materials
Three Pd-Cu-Ga dental alloys with very similar nominal compositions and dendritic as-cast microstructures were selected for study: Option (Ney Dental) and Spartan (Williams/lvoclar) contain a small amount of boron, while Spartan Plus (Williams/Ivoclar) is boron-free. Bars of each alloy were tested in tension for the as-cast and simulated porcelain-firing conditions, and values of mechanical properties were measured. Fracture surfaces and microstructures of axially sectioned and etched fracture specimens were observed with the scanning electron microscope (SEM). Except for the elastic modulus, significant differences were typically found in alloy properties. Heat treatment eliminated the dendritic microstructure, decreased strength and increased ductility. …
X-Ray Diffraction And Scanning Electron Microscopy Analyses Of A Gallium-Based Dental Restorative Alloy, Randa E. Shaker, William A. Brantley, Qiang Wu, John C. Mitchell
X-Ray Diffraction And Scanning Electron Microscopy Analyses Of A Gallium-Based Dental Restorative Alloy, Randa E. Shaker, William A. Brantley, Qiang Wu, John C. Mitchell
Cells and Materials
Specimens of a gallium-based dental alloy were prepared with different condensation techniques, with and without the removal of a surface layer, and after aging for 2 hours at 50°, 100° and 150°C. X-ray diffraction at times ranging from 10 minutes to 1 day showed the development of the four matrix phases (ß-Sn, CuGa2, Ga28Ag72, and In4Ag9) during the setting reaction. Scanning electron microscope (SEM) examination of specimens loaded to failure revealed brittle fracture, with greater porosity for hand-condensed specimens, and provided insight into crack propagation processes. Aging increased …
Effects Of Casting Conditions And Annealing On Microstructures And Vickers Hardness Of Dendritic Pd-Cu-Ga Dental Alloys, William A. Brantley, Qiang Wu, Zhuo Cai, Stanley G. Vermilyea, John C. Mitchell, Michael C. Comerford
Effects Of Casting Conditions And Annealing On Microstructures And Vickers Hardness Of Dendritic Pd-Cu-Ga Dental Alloys, William A. Brantley, Qiang Wu, Zhuo Cai, Stanley G. Vermilyea, John C. Mitchell, Michael C. Comerford
Cells and Materials
Three Pd-Cu-Ga alloys with as-cast dendritic microstructures and very similar compositions, two containing less than 1 wt% boron and the third boron-free, were cast with normal bench-cooling or rapid-quenching into water. Quenched specimens were also heat treated at temperatures of 1000°, 1200°, 1500° and 1800°F that span the firing cycles for dental porcelain. Similar values of Vickers hardness were observed for all three alloys, suggesting little effect from boron on yield strength. The hardness was relatively insensitive to the experimental conditions, except for heat treatment at 1500° and 1800°F where significant softening occurred with transformation of the microstructure to Pd …