Engineering Commons^™

The Corrosion Inhibition Behavior Of Thermally Aged Chromate Conversion Coating Applied To Aerospace Aluminum 2219, Michelle Stephane Pierre

FIU Electronic Theses and Dissertations

NASA Kennedy Space Center’s technical standard for corrosion protection of space flight hardware provides guidance concerning temperature restrictions and exposure limits for processing unpainted chromate conversion coatings (CCC) for the Orion crew space vehicle as part of the Artemis program. The standard requires that all CCC treated flight hardware components be fully coated within seven days with a maximum storage time of seven days at ambient temperatures (much less time at higher temperatures). Currently, there is no literature nor qualified industry testing supporting the exposure limits set by the standard. The standard is quite restrictive to processing flight components. In …

Development Of Local And Global Corrosion Sensing Technique To Monitor Structural Behavior Of Prestressed Concrete Structures, Dewan Z. Hossain

FIU Electronic Theses and Dissertations

Corrosion of steel rebar in reinforced concrete structures is a concern for highway bridge owners. According to 2002 study by the Federal Highway Administration, ~15% of the highway bridges in the US are structurally deficient due to corrosion and have an estimated annual direct cost of $8.3 billion. Generally, in post-tensioned bridges, ducts filled with poor or incomplete grouting can allow the tendons to come into contact with water, leading to corrosion and fracture. Although new and improved procedures of grouting have been developed to reduce the instances of poor grouting, the problem of how to reliably inspect tendons on …

Corrosion Durability Of A Nano-Particle Enriched Zinc-Rich Coating System For Highway Steel Bridges, Saiada Fuadi Fancy

FIU Electronic Theses and Dissertations

Corrosion is a major concern for the long-term durability and structural integrity of steel components of highway bridges when unprotected. The application of protective coatings has been widely used for corrosion mitigation of atmospherically exposed structural steel. At present, the zinc-rich primer (ZRP) based three-coat system is widely used in the United States. The metallic zinc pigment ideally would provide corrosion resistance by sacrificial as well as barrier protection. The life of these coating systems is at best only half of the bridge design life. Furthermore, premature degradation may occur if there are flaws in the system due to improper …

Retrofitting Of Bridge Elements Subjected To Predominantly Axial Load Using Uhpc Shell, Mahsa Farzad

FIU Electronic Theses and Dissertations

In the United States, ~30% of the ~600,000 highway bridges are categorized as structurally deficient or functionally obsolete. These bridges should be replaced or upgraded to sustain the transportation needs of the growing public and private sectors of the U.S. economy. It is not uncommon for structures to have advanced levels of corrosion-induced damage where major repair and maintenance works are required. However, the transportation infrastructure may undergo disruption during rehabilitation causing interruption to critical economic public, civil and commercial activities. This mandates the development of new techniques and materials for accelerated rehabilitation and resilience. To address this issue, a …

Corrosion Degradation Mechanism Of Cbpc Coating System For Highway Bridge Steel Components, Md Ahsan Sabbir

FIU Electronic Theses and Dissertations

Coatings are widely used to mitigate corrosion of structural steel in aggressive humid environments. However, the service life is often diminished in aggressive environments. Repair of coatings can be costly due to materials, labor and environmental controls. So, in search for novel coatings, Chemically Bonded Phosphate Ceramic (CBPC) coating was investigated for marine bridge application. The research on CBPC coating considered various exposure environments such as inland, beach, salt-fog, wet and alternate wet and dry exposure to identify the degradation mechanism. To assess the corrosion damage, the coating was evaluated by visual inspection, thickness, adhesion, microscopy and X-ray diffraction.

The …

On The Role Of The Pore Water Chemistry Of Deficient Post-Tension Grout To Promote Steel Corrosion, Samanbar Permeh

FIU Electronic Theses and Dissertations

Corrosion failure of post-tension tendons with pre-packaged thixotropic grout was documented in Florida Bridges in less than 10 years of service. Analysis of deficient grout in Florida post-tensioned (PT) bridges where severe corrosion developed indicated enhanced sulfate ion concentration, high pore water pH, enhanced moisture and low chloride content. The corrosion wasn’t consistent with the conventional causes of steel corrosion such as bleed water accumulation in grout void spaces, chloride contamination and pore water carbonation. Corrosion development was associated with deficient grout with enhanced sulfate levels. However, limited information is available on the corrosion behavior of PT strand in grout …

Evaluation Of Organic Protective Coatings As Corrosion Prevention For The Interior Of Subsea Pipelines In Sour Gas Service, Faris M. Alkordy

FIU Electronic Theses and Dissertations

The purpose of this study was to examine the performance of several generic types of organic protective coatings as a corrosion protection method for the interior of subsea pipelines in sour gas media. The sour gas environment was simulated in the laboratory by the use of an Autoclave and the performance of the organic coatings was studied via the use of Electrochemical Impedance Spectroscopy (EIS) and Linear Polarization Resistance (LPR) tests to determine the coatings resistance, capacitance and corrosion behavior before and after the exposure to sour gas environment. The coating degradation and the corrosion products formed were examined by …

The Microstructure And The Electrochemical Behavior Of Cobalt Chromium Molybdenum Alloys From Retrieved Hip Implants, Christopher P. Emerson

FIU Electronic Theses and Dissertations

Because of their excellent mechanical, tribological, and electrochemical properties, Cobalt Chromium Molybdenum alloys have been used as the material for both the stem and head of modular hip implants. Corrosion is one mechanism by which metal debris, from these implants, is generated, which can lead to adverse events that requires revision surgery. Manufacturing process such as wrought, as-cast, and powder metallurgy influences the microstructure, material properties, and performance of these implants

The current research focuses on analyzing the microstructure of CoCrMo alloys from retrieved hip implants with optical and scanning electron microscopy. Additionally, energy disperse spectroscopy was utilized to determine …

In-Vivo Corrosion And Fretting Of Modular Ti-6al-4v/Co-Cr-Mo Hip Prostheses: The Influence Of Microstructure And Design Parameters, Jose Luis Gonzalez Jr

FIU Electronic Theses and Dissertations

The purpose of this study was to evaluate the incidence of corrosion and fretting in 48 retrieved titanium-6aluminum-4vanadium and/or cobalt-chromium-molybdenum modular total hip prosthesis with respect to alloy material microstructure and design parameters. The results revealed vastly different performance results for the wide array of microstructures examined. Severe corrosion/fretting was seen in 100% of as-cast, 24% of low carbon wrought, 9% of high carbon wrought and 5% of solution heat treated cobalt-chrome. Severe corrosion/fretting was observed in 60% of Ti-6Al-4V components. Design features which allow for fluid entry and stagnation, amplification of contact pressure and/or increased micromotion were also shown …

An Investigation On Biocompatibility Of Bio-Absorbable Polymer Coated Magnesium Alloys, Sushma Amruthaluri

FIU Electronic Theses and Dissertations

Advances in biomaterials have enabled medical practitioners to replace diseased body parts or to assist in the healing process. In situations where a permanent biomaterial implant is used for a temporary application, additional surgeries are required to remove these implants once the healing process is complete, which increases medical costs and patient morbidity. Bio-absorbable materials dissolve and are metabolized by the body after the healing process is complete thereby negating additional surgeries for removal of implants.

Magnesium alloys as novel bio-absorbable biomaterials, have attracted great attention recently because of their good mechanical properties, biocompatibility and corrosion rate in physiological environments. …

An Assessment Of Novel Biodegradable Magnesium Alloys For Endovascular Biomaterial Applications, Dharam Persaud-Sharma

FIU Electronic Theses and Dissertations

Magnesium alloys have been widely explored as potential biomaterials, but several limitations to using these materials have prevented their widespread use, such as uncontrollable degradation kinetics which alter their mechanical properties. In an attempt to further the applicability of magnesium and its alloys for biomedical purposes, two novel magnesium alloys Mg-Zn-Cu and Mg-Zn-Se were developed with the expectation of improving upon the unfavorable qualities shown by similar magnesium based materials that have previously been explored. The overall performance of these novel magnesium alloys has been assessesed in three distinct phases of research: 1) analysing the mechanical properties of the as-cast …