Engineering Commons^™

Corrosion Of Oil Pipeline: A Case Study On The Niger Delta Region Of Nigeria., Victor U. Okoro

Corrosion Research

Corrosion of oil pipelines in Nigeria, particularly in the Niger Delta region, has extensive and detrimental environmental and societal impacts. This issue results in substantial financial losses and reputational damage for oil companies operating in the area. Local communities suffer economically, affecting agriculture and food security. Furthermore, corrosion-related oil spills lead to air quality degradation by releasing volatile organic compounds and greenhouse gases, contributing to respiratory issues and worsening climate change.

These oil spill cleanups are costly and time-consuming, with estimated expenses reaching billions of dollars. Using the Nembe Creek Trunk Line (NCTL) case study, it is evident that addressing …

Corrosion Case Study On Pipeline, Kangze Ren

Corrosion Research

The Kashagan pipeline leaks were likely caused by sulfur stress corrosion cracking, a combined corrosion mechanism developed by the presence of high pressure, the high level of hydrogen sulfide(the main "ingredient" of sour gas), and poor metallurgical choice. Improper welding and poor metallurgical examination were blamed for causing the leaking issue. The purpose of the current review is to raise the alarm about the inappropriate corrosion management of Kashagan oil production and its societal and environmental consequences.

The Study Of Corrosion On Additive-Manufactured Metals., Braydan Daniels

Electronic Theses and Dissertations

The purpose of this study was to investigate and compare the corrosion mechanisms between wrought and additive-manufactured (3D-printed) copper and stainless steel. The experimental procedure consisted of measuring the open circuit potential, electrochemical impedance spectroscopy, linear sweep voltammetry, Tafel analysis, surface topology, and scanning electron microscopy for each metal within salt water, tap water, sulfuric acid, and synthetic body fluid (excluding copper in synthetic body fluid).

Overall, printed stainless steel was more corrosion-resistant than wrought stainless steel in tap water and synthetic body fluid based on OCP, LSV, and surface topology results. Additionally, printed copper was more corrosion-resistant than wrought …

Surface Corrosion Response Of Al Alloys A383 And Aural 2 With Ce Additions In Aqueous Nacl And Salt-Fog Environments, Michael James Thompson

Masters Theses

Copper is commonly used in aluminum alloys to increase its strength by solid solution and precipitation strengthening, however, the corrosion resistance is inversely related to the amount of copper in the alloy. Over 70 percent of material used to produce aluminum alloys in the US come from recycled (secondary) alloys, many of which have a copper content of more than one percent by weight. Alloys with tightly controlled tolerances, where copper is seen as an impurity, are unable to utilize many of the recycling feedstock without adding newly processed (primary) aluminum to dilute impurities to within specifications. Primary aluminum is …

Intergranular And Pitting Corrosion Mechanisms Of Sensitized Aluminum Alloy Aa5083, Clayton Egleston

Williams Honors College, Honors Research Projects

The motivation and objectives of this project is to examine the mechanisms of intergranular corrosion (IGC) and pitting corrosion of sensitized AA5083. In this regard, different characterization techniques were used, including optical analysis of microstructure, cyclic potentiodynamic polarization with Tafel fitting, electrochemical impedance spectroscopy with electrical equivalent circuit (EEC) fitting, and potentiostatic current transient monitoring. The transition from IGC to pitting corrosion occurs when the grain boundaries become saturated with the β-phase (Mg₂Al₃). It was found that AA5083 becomes more vulnerable to pitting corrosion as the degree of sensitization increases.

Near-Ir Laser Ablation Of Simulated Radiologically Contaminated Oxides On Carbon Steel Feeder Pipes, Thao Viet Do

Electronic Thesis and Dissertation Repository

As nuclear power plants age and retire from service, many countries face significant challenges concerning the safe long-term storage and disposal of large volumes of low and intermediate level radioactive wastes (L&ILW). The volumes of metallic waste are of particular concern, as when metal corrodes it produces hydrogen that could lead to pressure build-up in interim storage and disposal. In Canada, a significant fraction of the metallic wastes for Canada Deuterium Uranium (CANDU) nuclear reactors are out-of-core reactor components, such as carbon steel (CS) feeder pipes. The radioactive contamination is expected to be largely confined to the surface oxide layers …

Electrochemical Impedance Spectroscopy Analysis Of Corrosion Of Reinforcing Steel In Fly Ash Mortar By Means Of Transmission Line Modeling, Padraig Stack

Williams Honors College, Honors Research Projects

Electrochemical impedance spectroscopy (EIS) is an important non-destructive tool that allows for a deeper understanding of the electrochemical processes and mechanisms occurring in an electrochemical cell. Equivalent electrical circuits (EECs) are used to model the impedance data into electrical components, such as resistors and capacitors, on a circuit. Current potentiostat offers software packages that can analyze the frequency response, but the software only supports “simple” EEC that can be written as fixed electrical components in some combination of series and parallel. Park and Macdonald propose a transmission line model (TLM) that does not use lumped-element models, instead, the values of …

Novel And Fast Peridynamic Models For Material Degradation And Failure, Siavash Jafarzadeh

Department of Mechanical and Materials Engineering: Dissertations, Theses, and Student Research

Fracture is one of the main mechanisms of structural failure. Corroded surfaces with chemically-induced damage are, notably, potential sites for crack initiation and propagation in metals, which can lead to catastrophic failure of structures. Despite some progress in simulating fracture and damage using classical models, realistic prediction of complex damage progression and failure has been out of reach for many decades. Peridynamics (PD), a nonlocal theory introduced in 2000, opened up new avenues in modeling material degradation and failure. Existing numerical methods used to discretize PD equations, however, are quite expensive as the PD nonlocal interactions make them unaffordable for …

Increasing The Corrosion Protection Of Aisi 1008 Carbon Steel By Surface Treatment With Unmodified And Benzotriazole Modified Sol-Gel Films, Shane Thomas Kelliher

Williams Honors College, Honors Research Projects

The corrosion performance of sol-gel coated AISI 1008 carbon steel was investigated in 3.5 wt% NaCl solutions of pH 7, 9, and 12 using electrochemical measurements. A corrosion inhibitor, benzotriazole (BTA) was added to the sol-gel mixture and tested as a second, modified sol-gel coating. Sol-gel films adhered evenly to metal samples and were characterized by FTIR spectroscopy. Electrochemical Impedance Spectroscopy (EIS) showed an increase in polarization resistance from blank to sol-gel coated samples (600-18,800,000 ohms). Cyclic polarization (CPP) curves showed positive hysteresis loops for blank and unmodified sol-gel coated samples which increased at high pH following the backward potential …

Aqueous Redox Flow Batteries With Boron Doped Diamond As An Electrode., Alex M. Bates

Electronic Theses and Dissertations

As the interest and implementation of renewable energy accelerates, so does that of grid energy storage. It is widely believed that a cost-effective energy storage technology will bring about the proliferation of renewable energy. Redox flow battery (RFB) technology represents a promising solution to cost-effective grid energy storage. Compared to other technologies, RFBs have a long lifetime, high efficiency, are non-flammable, significantly reduce cost, and separately scale power and energy. The separation of power and energy enables increased energy capacity by simply adding electrolyte volume. Of the challenges facing RFB technology, one readily apparent is the cost of the active …

A Study And Simulation Of Flux Induced Corrosion In Copper Tubing Used For The Distribution Of Potable Water, Daniel O. Benham

Materials Engineering

Water side corrosion within copper plumbing can occur due to a wide variety of unwanted circumstances. Through the controlled immersion of six ¾” copper tubing samples with five utilizing a unique industry standard soldering flux, this investigation associates residual flux deposits with the initiation of pitting in copper. Water stagnation in a copper potable water distribution system, typically associated with an infrequently used faucet, is a condition highly prone to copper pitting. A test apparatus designed to produce a partially stagnant flow condition with scheduled electrolyte flushes every 3 days was developed and constructed to contain 6 test samples for …

Benefits Of Aluminum: Comparing The Common Materials In The Bar Grating Industry, Joanthan Geiser

Williams Honors College, Honors Research Projects

The main aim of this project is to study the wholistic behavior of the 6xxx series of aluminum for use in the bar grating industry for a waste water treatment environment. This project will study the comparison of certain aluminum 6xxx series alloys to steel, stainless steel, and glass fiber-reinforced plastic. While comparing these materials, it will look at the mechanical properties such as modulus of elasticity, yield strength, and ultimate tensile strength. In addition, the available corrosion test of the 6xxx series aluminum alloys will be examined to find a generalization of the corrosion behavior for this series. A …

Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla

Publications

Reinforced Concrete (RC) structures are vital to the US’s civil infrastructure for their strength and versatility. Unfortunately, RC elements deteriorate rapidly when exposed to corrosive environments. One possible solution is to extend the life of RC elements and systems using microencapsulated corrosion inhibitors to reduce the rebar corrosion rate. The capsules house an anodic corrosion inhibitor agent including calcium nitrate (CN) and triethanolamine (TEA). The integration of such microencapsulated materials will enhance the durability and extend the useful life by controlling the corrosion precursors and the corrosion process during damage evolution. Therefore, this work aims to develop and characterize the …

The Influence Of Organic Pigments On Coating Properties, Sarah Medeiros

Williams Honors College, Honors Research Projects

Abstract

The purpose of this project was to identify the qualities of two synthesized organic pigments added to a coating. These high-performance pigments were benzodipyrrolidone and benzodifuranone, which are π-conjugated monomers. These pigments were each formulated into two different pigment concentrations and compared with a control that had no pigment. This project is limited by time constraints and the number of variables that can be tested in that time. Performance testing was conducted to evaluate the qualities of these coatings. The results demonstrated that the coatings were reproducible and most tests had results that were equal to or exceeded the …

Comparison Of Intrusive And Non-Intrusive Methods For Corrosion Monitoring Of Fuel Processing Systems, Armando Jacob Espinoza, Thomas Conner Field

Materials Engineering

This presentation contains an assessment of the best overall corrosion monitoring device, intrusive or non-intrusive, for use in the petrochemical industry. Corrosion in the petrochemical industry is a large issue because it causes a deterioration of pipe integrity in fuel processing systems. A reduction of pipe wall integrity due to corrosion could result in a leak or an explosion of fuel processing lines since those systems function at high pressures. The use of corrosion monitoring systems in the petrochemical industry helps to detect early signs of corrosion prior to failure so that proper maintenance can be performed to prevent catastrophe. …

Pitting Corrosion Of 410 Stainless Steel In Hcl Solutions, Paul D. Krell

Williams Honors College, Honors Research Projects

410 stainless steel (SS) is a material used in HCl services, such as distillation column trays in oil refineries. Unlike other alloys, however, the oil refining industry lacks a good reference for the corrosion rate of 410 SS at the varying HCl concentrations and temperatures the material might experience as trays in crude unit distillation columns. The goal of this project is to fill that knowledge gap. The corrosion behavior of 410 SS in HCl environments of pH 0.50, 1.25, 2.25, 3.25, and 4.25 at temperatures of 38, 52, 79, and 93°C was investigated using several methods. Cyclic potentiodynamic polarization …

The Effects Of Carboxylic Acids In Aluminum Anodizing, Abby E. Koczera

Honors Theses and Capstones

Hard-anodized alumina coatings were formed in sulfuric acid at low temperature and high current density in the presence of carboxylic acid additives. Citric acid, trimesic acid, mellitic acid and ethylenediaminetetraacetic acid (EDTA) were utilized in varying concentrations. The additives were chosen for their capacity to form complexes with tri-valent aluminum and hence impart chemical stability to the coatings. The coatings were sealed in boiling water, and corrosion resistance was observed in a high pH solution of potassium hydroxide. The coatings were examined using scanning electron microscopy (SEM) to assess coating thickness and pore dimensions. Thicker coatings were produced when the …

Galvanic Corrosion On Monel K-500 And 1018 Carbon Steel Couple, John K. Nnyanzi

Williams Honors College, Honors Research Projects

The purpose of this research project was to evaluate galvanic damage on 1018 Carbon Steel coupled to Monel K-500 at varying rotation speeds on a rotating cylinder electrode in an aerated solution of ASTM artificial seawater. The work in this project is and attempt to study corrosion behavior for a Monel fastener coupled to a Carbon Steel plate. Polarization curves of each material at different rotation speeds were created to predict the corrosion behavior for a galvanic couple of Carbon Steel and Monel. The Potentiodynamic sweeps predict an increase in the corrosion current density for the galvanic couple when then …

Oxidation Resistance Of Nanocrystalline 316l Stainless Steel Processed By High Pressure Torsion, Kevin J. Meisner

Williams Honors College, Honors Research Projects

High Pressure Torsion (HPT) is a materials processing method used to refine the grain size of metallic materials through the application of simultaneous axial and torsional strain. HPT is reported to result in nanocrystalline structure, which the current scientific literature suggests may improve the high temperature oxidation resistance by enhancing diffusion of solutes, particularly Cr, to the surface to form a protective external oxide scale. If oxidation resistance is improved, this possibly allows the use of 316L in oxidizing environments where more expensive alloys are typically used. However, the influence of grain refinement to nanoscale on various properties have been …

Evaluation Of Organic Protective Coatings As Corrosion Prevention For The Interior Of Subsea Pipelines In Sour Gas Service, Faris M. Alkordy

FIU Electronic Theses and Dissertations

The purpose of this study was to examine the performance of several generic types of organic protective coatings as a corrosion protection method for the interior of subsea pipelines in sour gas media. The sour gas environment was simulated in the laboratory by the use of an Autoclave and the performance of the organic coatings was studied via the use of Electrochemical Impedance Spectroscopy (EIS) and Linear Polarization Resistance (LPR) tests to determine the coatings resistance, capacitance and corrosion behavior before and after the exposure to sour gas environment. The coating degradation and the corrosion products formed were examined by …

In-Vivo Corrosion And Fretting Of Modular Ti-6al-4v/Co-Cr-Mo Hip Prostheses: The Influence Of Microstructure And Design Parameters, Jose Luis Gonzalez Jr

FIU Electronic Theses and Dissertations

The purpose of this study was to evaluate the incidence of corrosion and fretting in 48 retrieved titanium-6aluminum-4vanadium and/or cobalt-chromium-molybdenum modular total hip prosthesis with respect to alloy material microstructure and design parameters. The results revealed vastly different performance results for the wide array of microstructures examined. Severe corrosion/fretting was seen in 100% of as-cast, 24% of low carbon wrought, 9% of high carbon wrought and 5% of solution heat treated cobalt-chrome. Severe corrosion/fretting was observed in 60% of Ti-6Al-4V components. Design features which allow for fluid entry and stagnation, amplification of contact pressure and/or increased micromotion were also shown …

Combinatorial Approach To Turbine Bond Coat Discovery, Christopher Metting, Johnathan Bunn, Ellen Underwood, Stephen Smoak, Jason Hattrick-Simpers

Jason R. Hattrick-Simpers

No abstract provided.

The Examination Of Stress Corrosion Cracking In High Strength Carbon Steel Through Combined Mechanical-Electrochemical Testing, Jacob Sines

Williams Honors College, Honors Research Projects

Through the analysis of materials and environments seen in industry a better understanding of the fundamentals behind degradation mechanisms can be observed. The scope of this project was to better understand the fundamentals behind the degradation of high strength pipeline steels in a lab setting to simulate an environment seen in industry. Specifically the degradation mechanisms of high and nearly neutral pH stress corrosion cracking were examined in environments that simulated oil and gas pipelines buried in soil. Experimentation was carried out utilizing X65 carbon steel specimen, a Gamry potentiostat, a CORTEST proof ring, a CORTEST slow strain rate machine, …

Surface Modification Of Aluminum Alloys By Plasma Electrolytic Oxidation, Vahid Dehnavi

Electronic Thesis and Dissertation Repository

Plasma Electrolytic Oxidation (PEO) is a surface treatment for the production of ceramic oxide coatings with great properties, such as high wear and corrosion resistance, on metal substrates, particularly aluminum and magnesium alloys. Formation of PEO coatings involves complex processes and mechanisms that are difficult to study. Currently, the PEO process is in a transition phase from research to commercial application, with a primary focus on the corrosion and wear protection of light alloys, and has recently generated interest as a promising surface treatment for biomedical applications.

To justify the industrial application of PEO, a more systematic and in-depth study …

Magnesium-Titanium Alloys For Biomedical Applications, Ilona Hoffmann

Theses and Dissertations--Chemical and Materials Engineering

Magnesium has been identified as a promising biodegradable implant material because it does not cause systemic toxicity and can reduce stress shielding. However, it corrodes too quickly in the body. Titanium, which is already used ubiquitously for implants, was chosen as the alloying element because of its proven biocompatibility and corrosion resistance in physiological environments. Thus, alloying magnesium with titanium is expected to improve the corrosion resistance of magnesium.

Mg-Ti alloys with a titanium content ranging from 5 to 35 at.-% were successfully synthesized by mechanical alloying. Spark plasma sintering was identified as a processing route to consolidate the alloy …

Corrosion Of Stainless Steel 316l And Astm F75 Cobalt Chromium Alloy During Immersion Testing In Silver Salt Solutions, Meagan Higgins

Materials Engineering

This study evaluates the potential effects of silver salts on biocompatible metals used for prostheses during the chemical reduction process to produce a silver antimicrobial layer on the metal’s surface. Samples of two biocompatible metals were obtained: Stainless Steel 316L and ASTM F75 Cobalt Chromium Alloy. Three different silver salts were also acquired: silver nitrate, silver sulfadiazine, and silver chloride. Specimens of each metal were cut to size using a 4-1/2 inch aluminum oxide, 40 grit, cut off wheel for metal, attached to a Dewalt Angle Grinder. The biocompatible metal samples were then subject to either Solution 1, water with …

Analyzing The Corrosion Resistance Of Ni-Shield 200 Coatings At Different Temperatures When Exposed To Sulphuric Acid, Alex Hussinger

Materials Engineering

Six steel samples each were twin wire arc sprayed with Hastelloy C-276 or Nickel-Shield 200 coatings approximately 0.020″ thick. These samples were then cut into 3″ by 3″ squares. A 2″ diamond grit hole saw was used to abrade and polish to a smooth surface a ring in the middle in order to get an O-ring mechanical seal. The samples were then weighed and loaded into a jig that started from the bottom up with a stainless steel plate, then the sample, then a Viton O-ring, a ¾″ thick glass plate with a 1 3/4″ hole cut in it, another …

The Effects Of Heat Treatment On Area Percent Porosity And Corrosion Behavior Of High-Nickel Thermal Spray Coatings, Travis Crowe, Alec Guraydin

Materials Engineering

Samples of two Thermal Spray Coating (TSC) alloys on a low carbon steel substrate were obtained: alloy C276 and Nicko-Shield 200. Specimens of each alloy were subjected to heat treatments at temperatures at 1100° for 60 minutes and 1200° for 10 minutes, with some specimens left in the as-sprayed condition. Three replicates were prepared for each condition. Thin 1” strips were cut using a diamond wafering blade for porosity measurements and 2” x 1” specimens were cut for corrosion testing using a SiC abrasive saw. The porosity specimens were mounted in acrylic resin, polished, and examined using SEM. From these …

Tribological Comparison Of Traditional And Advanced Firearm Coatings, Greg Boban

Master's Theses

The objective of this project is to find which type of coating has the best performance characteristics for finishing firearms. This is accomplished by measuring and comparing several performance characteristics, such as: adhesion, hardness, wear resistance, friction control, and corrosion resistance. Appearance is not a factor since any exterior coating that is flashy can be subdued or camouflaged with special purpose paints, which have proven durable enough for such purposes. Cost will not be a limiting factor for this experiment, but will be discussed in the conclusion as a secondary concern. This data will be used to identify the best …

Effectiveness Of Thermal Oxidation In Relation To Anterior Cervical Plates, Katherine A. Miyashiro

Master's Theses

Ti-6Al-4V anterior cervical plates (ACP) are used in spinal fusion surgeries to fixate cervical vertebrae during graft adhesion. However, documented cases of implant failure and the potential for ACP corrosion raise concerns regarding any degradation of material resulting from extended implantation. In addition, abrasion during implantation may damage a section of the protective oxide layer, potentially exposing surrounding tissues to the harmful effects of bare titanium, aluminum, and vanadium. Thermal oxidation has been shown to improve corrosion-resistance and wear-resistance, depending on temperature and time. To quantify the attributes of the thermally grown oxide layer, Ti-6Al-4V coupons underwent thermal oxidation treatments …