Investigation Of Through Thickness Microstructure And Mechanical Properties In Friction Stir Welded 7n01 Aluminum Alloy Plate, Xingxin Zhao, Zhiyong Yang, Joseph P. Domblesky, Jianmin Han, Zhiqiang Li, Xiaolong Liu
Investigation Of Through Thickness Microstructure And Mechanical Properties In Friction Stir Welded 7n01 Aluminum Alloy Plate, Xingxin Zhao, Zhiyong Yang, Joseph P. Domblesky, Jianmin Han, Zhiqiang Li, Xiaolong Liu
Mechanical Engineering Faculty Research and Publications
An on-going problem in friction stir welded (FSW) joints used in the high-speed train sector is that the microstructure and mechanical properties can significantly vary in thick sections. Because inhomogeneous properties can reduce weld efficiency and degrade service performance, it is of some interest to understand how inhomogeneous properties can develop in FSW welds made from precipitation hardening alloys such as 7N01. In the current study, butt welds were made using 12 mm thick plates and then sectioned perpendicular to the weld line. Five 2.2 mm thick slices were cut from a section and used to measure tensile properties access …
Mechanical Characterizations Of 3d-Printed Plla/Steel Particle Composites, Hozhabr Mozafari, Pengfei Dong, Haitham Hadidi, Michael P. Sealy, Linxia Gu
Mechanical Characterizations Of 3d-Printed Plla/Steel Particle Composites, Hozhabr Mozafari, Pengfei Dong, Haitham Hadidi, Michael P. Sealy, Linxia Gu
Department of Mechanical and Materials Engineering: Faculty Publications
The objective of this study is to characterize the micromechanical properties of poly-L-lactic acid (PLLA) composites reinforced by grade 420 stainless steel (SS) particles with a specific focus on the interphase properties. The specimens were manufactured using 3D printing techniques due to its many benefits, including high accuracy, cost effectiveness and customized geometry. The adopted fused filament fabrication resulted in a thin interphase layer with an average thickness of 3 μm. The mechanical properties of each phase, as well as the interphase, were characterized by nanoindentation tests. The effect of matrix degradation, i.e., imperfect bonding, on the elastic modulus of …