Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Aaa Task-4 Quarterly (September 1 – November 30, 2001) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including HT- 9, EP 823 and 422. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these alloys will be evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. The extent and morphology of cracking of these alloys will further be evaluated …

Analysis Of Corrosion Of Steel By Lead Bismuth Eutectic, John Farley, Dale L. Perry

Transmutation Sciences Materials (TRP)

We examined stainless samples that were exposed to LBE in experiments conducted by the Russians, under contract to Los Alamos. We examined both corroded and uncorroded samples using the Scanning Electron Microscope (SEM), the Energy Dispersive X-Ray (EDAX) Spectroscopy, and the X-ray Photoelectron Spectrometer (XPS). We found that the surface of the corroded sample is covered by oxygen-containing compounds, presumably mostly iron oxide. In samples exposed for shorter times or lower temperatures, we found that some areas were covered by an oxide layer, and some areas was uncovered. We found that the level of Cr in the uncovered area is …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics: Quarterly Progress Report August 16,2001- November 15, 2001, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the AAA proposed application.

Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with very limited density. The transport of oxygen and corrosion products, their interaction and variation of corrosion/precipitation along the flow are not well understood.

The first subtask of this project involves using a …

Analysis Of Corrosion Of Steel By Lead Bismuth Eutectic, John Farley, Dale L. Perry

Transmutation Sciences Materials (TRP)

The goal is to achieve a basic understanding of the corrosion of stainless steel by Lead Bismuth Eutectic (LBE), which has been proposed for use in the transmuter as both a coolant and as a sputtering target.

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The proposed work will combine chemical kinetics and hydrodynamics in target and test-loop lead-bismuth eutectic (LBE) systems to model system corrosion effects. This approach will result in a predicative tool that can be validated with corrosion test data, used to systematically design tests and interpret the results, and provide guidance for optimization in LBE system designs. The task includes of two subtasks. The first subtask is to try to develop the necessary predictive tools to be able to predict the levels of oxygen and corrosion products close to the boundary layer through the use of Computational Fluid Dynamics (CFD) modeling. …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems, Brendan O'Toole, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this project is to evaluate the effect of hydrogen on cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The test materials will undergo appropriate thermal treatments prior to being hydrogen-charged by potentiostatic cathodic polarization technique in a simulated aqueous environment at different temperatures of interest. The specimens, upon completion of testing, will be metallographically examined. Further, the scanning electron microscopy (SEM) will be used to determine the extent and nature of cracking in the specimens tested. The thrust of the proposed …