Experimental Investigation Of The Thermochemical Reduction Of Arsenite And Sulfate: Low Temperature Hydrothermal Copper, Nickel, And Cobalt Arsenide And Sulfide Ore Formation, Nicholas Allin

Graduate Theses & Non-Theses

Experiments were conducted to determine the relative rates of reduction of aqueous sulfate and aqueous arsenite (As(OH)₃,aq) using foils of copper, nickel, or cobalt as the reductant, at temperatures of 150ºC to 300ºC. At the highest temperature of 300°C, very limited sulfate reduction was observed with cobalt foil, but sulfate was reduced to sulfide by copper foil (precipitation of Cu₂S (chalcocite)) and partly reduced by nickel foil (precipitation of NiS₂ (vaesite) + NiSO₄·xH₂O). In the 300ºC arsenite reduction experiments, Cu₃As (domeykite), Ni₅As₂, or CoAs (langisite) …

Effect Of Support, Preparations Methods, Ag Promotion And Nc Size On The Activity, Selectivity And Sintering Deactivation Of Supported Co Fischer-Tropsch Catalyst, Mahmood Rahmati

Theses and Dissertations

A series of silver-promoted, 20 wt% cobalt Fischer-Tropsch synthesis (FTS) catalysts supported on an alumina modified with 5 wt% silica were prepared using two methods: traditional incipient wetness impregnation (IWI) and a new solvent-deficient precipitation (SDP) technique. Catalysts containing silver promoter concentrations of 0.3, 0.6, 1.2, and 2.5 wt% were prepared using each of the two methods. Silver improved the reducibility of the cobalt significantly, lowering reduction temperatures by up to 100°C, and increasing the extent of reduction by up to 35%. Further, in both preparation methods, changing the silver loading altered the cobalt dispersion. The smallest Co crystallite size …

Synthesis And Applications Of Ceramic (Silicon Carbide And Silicon Nitride), Metallic (Cobalt(0)) And Polymeric (Polyurethane) Aerogels, Parwani M. Rewatkar

Doctoral Dissertations

"A new method has been demonstrated for the synthesis of monolithic ceramic and purely metallic aerogels from xerogel powder compacts, and the use of polyurethane aerogels based on cyclodextrins as efficient desiccants.

I. Highly porous ( > 80%) monolithic SiC and Si₃N₄, aerogels were prepared from compressed compacts of polyurea-crosslinked silica xerogel powders. The process is time efficient as solvent-exchange through powders is fast, and energy efficient as it bypasses drying with supercritical fluids. The final ceramic objects were chemically pure, sturdy, with compressive moduli at 37 ±7 MPa and 59 ± 7 MPa, and thermal conductivities …