Open Access. Powered by Scholars. Published by Universities.®
- Discipline
Articles 1 - 5 of 5
Full-Text Articles in Engineering
Swelling-Etching Characterization Of Copper (I) Oxide - Pdms For The Development Of Micro/Nano - Particles Composite Mems Corrosion Sensor, Abdoul Kader Maiga
Swelling-Etching Characterization Of Copper (I) Oxide - Pdms For The Development Of Micro/Nano - Particles Composite Mems Corrosion Sensor, Abdoul Kader Maiga
Graduate Theses and Dissertations
The primary objective for this thesis is to contribute to the understanding of the oxide removal process for a corrosion sensing device. The goal for designing such a device is for monitoring corrosion on metallic structures. The sensing material (6.35mm x 1mm discs) of the device is composed of copper (I) oxide particles mixed in some polydimethylsiloxane (PDMS). The PDMS, “housing,” is meant for controlling the oxidation rate through the sensing material. A solvent was used to facilitate the etchant diffusion through the PDMS matrix. Toluene and acetic acid were the ideal solvent and etchant, respectively, for carrying out the …
Creep Of Sylramic-Ibn Fiber Tows At Elevated Temperature In Air And In Silicic Acid-Saturated Steam, Kevin B. Sprinkle
Creep Of Sylramic-Ibn Fiber Tows At Elevated Temperature In Air And In Silicic Acid-Saturated Steam, Kevin B. Sprinkle
Theses and Dissertations
Stressed oxidation experiments on Sylramic-iBN fiber tows were performed to evaluate the novel fiber's mechanical performance, creep behavior, and creep mechanisms. This research effort investigated creep response of Sylramic-iBN fiber tows at elevated temperatures in both air and in silicic acid-saturated steam environments. Creep experiments were conducted at creep stresses ranging from 127 to 762 MPa at 400°C and 500°C in order to examine the mechanical behavior of the Sylramic-iBN fiber tows at temperatures below and above the melting point of boria (450°C). Sylramic-iBN fibers are known to have excellent creep resistance, better than most other non-oxide fibers and significantly …
Tension-Compression Fatigue Of An Oxide/Oxide Ceramic Matrix Composite At Elevated Temperature In Air And Steam Environments, Richard L. Lanser
Tension-Compression Fatigue Of An Oxide/Oxide Ceramic Matrix Composite At Elevated Temperature In Air And Steam Environments, Richard L. Lanser
Theses and Dissertations
Tension-compression fatigue behavior of an oxide-oxide ceramic matrix composite was investigated at 1200°C in air and steam. The composite is comprised of an alumina matrix reinforced with Nextel 720 fibers woven in an eight harness satin weave. The composite relies on a porous matrix for damage tolerance. Compression and tension tests to failure were conducted to characterize basic mechanical properties. Tension-compression fatigue tests were performed at 1 Hz frequency with a ratio of minimum to maximum stress of -1. Maximum stresses ranged from 60-120 MPa. Fatigue run-out (defined as 105 cycles) was achieved in air at 80 MPa and in …
Effect Of Prior Exposure At Elevated Temperatures On Tensile Properties And Stress-Strain Behavior Of Three Oxide/Oxide Ceramic Matrix Composites, Christopher J. Hull
Effect Of Prior Exposure At Elevated Temperatures On Tensile Properties And Stress-Strain Behavior Of Three Oxide/Oxide Ceramic Matrix Composites, Christopher J. Hull
Theses and Dissertations
Thermal stability of three oxide-oxide ceramic matrix composites was studied. The materials studied were NextelTM610/aluminosilicate (N610/AS), NextelTM720/aluminosilicate (N720/AS), and NextelTM720/Alumina (N720/A), commercially available oxide-oxide ceramic composites (COI Ceramics, San Diego, CA). The N610/AS composite consists of a porous aluminosilicate matrix reinforced with laminated woven alumina N610 fibers. The N720/AS and N720/A composites consist of a porous oxide matrix reinforced with laminated, woven mullite/alumina (NextelTM720) fibers. The matrix materials are aluminosilicate in N720/AS and alumina in N720/A. All three composites have no interface between the fibers and matrix, and rely on the porous …
Fatigue Behavior Of Im7/Bmi 5250-4 Composite At Room And Elevated Temperatures, James T. Tipton
Fatigue Behavior Of Im7/Bmi 5250-4 Composite At Room And Elevated Temperatures, James T. Tipton
Theses and Dissertations
The tension-tension fatigue and tension-compression fatigue behaviors of the IM7/BMI 5250-4 composite were investigated. The tension-tension fatigue of the composite with 0/90 and ±45 fiber orientations was studied at 23, 170, and 190°C. The tension-compression fatigue of the composite with 0/90 fiber orientation was examined at 23°C. The tensile and compressive properties of the composite were also evaluated at room and elevated temperatures for both 0/90 and ±45 fiber orientations. Elevated temperature had little effect on the tensile properties of the 0/90 fiber orientation, but strongly influenced the ±45 tensile properties as well as the compressive properties of both fiber …