Fabrication Of Black Phosphorus Terahertz Photoconductive Antennas, Nathan Tanner Sawyers
Fabrication Of Black Phosphorus Terahertz Photoconductive Antennas, Nathan Tanner Sawyers
Physics Undergraduate Honors Theses
Terahertz (THz) photoconductive antennas (PCAs) using 40nm thin-film flakes of black phosphorus (BP) and hexagonal boron nitride (hBN) have been shown computationally to be capable of THz emission comparable to those based on GaAs [2]. In this paper, I briefly describe the scientific and practical interest in THz emissions and explain what warrants research into black phosphorus as a photoconductive semiconductor in THz devices. Furthermore, I outline the basic principle of how these antennas work and mention alternative designs produced by other researchers in the past. Finally, I summarize the fabrication process of these antennas, as well as the measurements …
Characterization Of Gesn Semiconductors For Optoelectronic Devices, Hryhorii Stanchu
Characterization Of Gesn Semiconductors For Optoelectronic Devices, Hryhorii Stanchu
Graduate Theses and Dissertations
Germanium-tin alloys with Sn compositions higher than 8 at. % to 10 at. % have recently attracted significant interest as a group IV semiconductor that is ideal for active photonics on a Si substrate. The interest is due to the fact that while at a few percent of Sn, GeSn is an indirect bandgap semiconductor, at about 8 to 10 at. % Sn, GeSn transitions to a direct bandgap semiconductor. This is at first surprising since the solid solubility of Sn in Ge under equilibrium growth conditions is limited to only about 1 at. %. However, under non-equilibrium growth conditions, …
Si-Based Germanium Tin Photodetectors For Infrared Imaging And High-Speed Detection, Huong Tran
Si-Based Germanium Tin Photodetectors For Infrared Imaging And High-Speed Detection, Huong Tran
Graduate Theses and Dissertations
Infrared (IR) radiation spans the wavelengths of the windows: (1) near-IR region ranging from 0.8 to 1.0 μm, (2) shortwave IR (SWIR) ranging from 1.0 to 3.0 μm, (3) mid-wave IR (MWIR) region covering from 3.0 to 5.0 μm, (4) longwave IR (LWIR) spanning from 8.0 to 12.0 μm, and (5) very longwave IR extending beyond 12.0 μm. The MWIR and LWIR regions are important for night vision in the military, and since the atmosphere does not absorb at these wavelengths, they are also used for free-space communications and astronomy. Automotive and defect detection in the food industry and electronic …
Proton Irradiation Effects On Semiconductor Cdse/Zns Core/Shell Nanocrystals, Stephen Graham Charter
Proton Irradiation Effects On Semiconductor Cdse/Zns Core/Shell Nanocrystals, Stephen Graham Charter
Graduate Theses and Dissertations
The absorbance and photoluminescence measurement of semiconductor CdSe/ZnS core shell nanocrystals were reviewed and investigated after they were exposed to proton irradiation. The CdSe/ZnS core shell nanocrystals of 3.2nm and 4.4nm were commercially purchased and investigated. These nanocrystals were embedded in UV resin. Proton irradiation of energy 2MeV was applied at doses from 3 x 1013 protons cm-2 to 1.47 x 1015 protons cm-2 for both nanocrystal sizes. Absorbance measurements were conducted at 300K. Results from absorbance measurements showed slight broadening of the first exciton peak of both samples but was most noticeable in the 3.2nm nanocrystal sample. UV resin …