An Analysis Of Microstructure And Corrosion Resistance In Underwater Friction Stir Welded 304l Stainless Steel, Tad Dee Clark
An Analysis Of Microstructure And Corrosion Resistance In Underwater Friction Stir Welded 304l Stainless Steel, Tad Dee Clark
Theses and Dissertations
An effective procedure and parameter window was developed for underwater friction stir welding (UWFSW) 304L stainless steel with a PCBN tool. UWFSW produced statistically significant: increases in yield strengths, decreases in percent elongation. The ultimate tensile strength was found to be significantly higher at certain parameters. Although sigma was identified in the UWFSWs, a significant reduction of sigma was found in UWFSWs compared to ambient FSWs. The degree of sensitization in UWFSWs was evaluated using double loop EPR testing and oxalic acid electro-etched metallography. Results were compared to base metal, ambient FSW, and arc welds. Upper and lower sensitization localization …