Materials Engineering

Tensile coupons of Ti-6Al-4V were heat treated at varying annealing temperatures from 1200°F (648°C) to 1450°F (787°C) at 50°F (23°C) increments for 1 hour. The samples were air cooled to room temperature or furnace cooled to 800°F (426°C) followed by air cooling to room temperature. Four tensile coupons were treated at each annealing temperature and cooling rate. Alpha case was observed to form on the surface of the samples post heat treatment with a maximum depth of 25 µm (.001 in). Samples were tensile tested for their ultimate tensile strength, yield strength, and percent elongation. Samples across all annealing temperatures …